Monovalent cation perm-selective membranes(MCPMs):New developments and perspectives☆

Liang Ge,Bin Wu,Dongbo Yu,Abhishek N.Mondal,Linxiao Hou,Noor Ul Afsar,Qiuhua Li,Tingting Xu,Jibin Miao,Tongwen Xu*

CAS Key Laboratory of Soft Matter Chemistry,Collaborative Innovation Center of Chemistry for Energy Materials,School of Chemistry and Materials Science,University of Science and Technology of China,Hefei 230026,China

1.Introduction

Ion exchange membranes(IEMs)are typically composed of hydrophobic polymer matrix,immobile charged ion exchange groups,and movable counter-ions.Since last century,IEMs as emerging materials for ion separation,have drawn significant attentions due to their wide applications in seawater desalination[1],environmental protection[2],resources recovery[3]and energy production[4].The extensive applications of IEMs further promote the investigations in both academic and industrial level.Meanwhile,new essential properties of traditional IEMs are proposed to satisfy the specific applications,e.g.,electrodialytic concentration of seawater to produce sodiumchloride[5],acid recovery in hydrometallurgy[6],removal of specific ions in liquid waste[7],and lithiumrecovery from brine[8,9].One of the generalissues in the abovementioned systems is the presence of monovalent cations and multivalent cations.In this case,perm-selective permeation of monovalentions through the membranes is indeed needed.Thereby,more efforts have been devoted towards the preparation of cation exchange membranes with perm-selectivity for monovalent cations[5,10-18].

As the name suggests,monovalent cation perm-selective membranes(MCPMs)allow the high permeation of monovalent cations,while retaining the selective passage of multivalent cations[19].Owning to the distinguished functions,MCPMs have been extensively investigated in different applications.Specifically,in this review the topics are mainly focused on electrodialysis(ED)and diffusional dialysis(DD)processes,although there are many other fields concerned with ionic separation/fractionation[17,20-22].

2.Mechanism of the Perm-selective Separation of MCPMs

Perm-selectivity of cations in a mixture through MCPMs is basically governed by their affinity towards the membranes(ion exchange equilibrium constant)and the migration speed in the membrane phase(mobility ratio among the cations)[12,13,19].Based on this universal rule,various mechanisms have been proposed to explain the permselective separation of the MCPMs,which were summed up as follows:(1)pore-size sieving effect decided by the different hydrated ionic radii,(2)electrostatic barrier effect due to the difference in electrostatic repulsion between monovalent cations and multivalent cations,and(3)hydration energy difference caused by the different Gibbs hydration energy of cations.

To simplify the system,Na+ion is generally used as a standard cation.When one equivalent of Na+ion permeates through MCPMs,the permeated equivalency of a given cation is evaluated.

where,tAandtNa+are the transport numbers of cations A and Na+in the membrane phase,whereasCAandCNa+show the concentration of cations A and Na+at the surface of membrane on desalting side of solution during electrodialysis,respectively.In fact,in order to calculate simply,the reported perm-selectivity in some studies is directly considered as the flux ratios ofNa+ion and cation A,especially when the feed solution contains equal concentrations of the two ions[24-26].

3.Traditional Technologies for Fabricating MCPMs

3.1.Covalent cross-linking

Perm-selective separation by pore-size sieving effect based on the polymeric network is firstly proposed according to the difference in hydrated ionic radius of ions.It is believed that covalent cross-linking technique is a promising way of improving both the compactness and chemical stability of MCPMs.The improved compactness of the membrane would lower the migration speed of cations and the ions with smaller hydrated ionic radii would easily pass through the membrane.For example,polycondensation of phenolsulfonatephenol-formaldehyde system[27]or sulfonation of copolymer membranes composed of styrene and divinylbenzene(DVB)[28]was adopted to fabricate MCPMs.The perm-selectivity increased remarkably with the content of cross-linking agent,which caused a decreasing pore size of the membranes.Specifically,the higher perm-selectivity was usually observed in the condensation-type membranes as compared to the copolymerization-type membranes.That is because ion exchange equilibrium constant of divalent cations to monovalent ions greatly increases—in the condensation-type membranes in contrast to the slight decrease in the copolymerization-type membranes[27].Sol-gel process under acidic condition is known as another approach to prepare MCPMs[29].The inorganic segment(silica)inside the poly(vinyl alcohol)matrix led to a more compact membrane structure,it was thereby very difficult for the bulkier cations to pass through,resulting in a high perm-selectivity,especially for Na+/Fe3+system(the perm-selectivity was approximately equalto 10).Generally,the covalent cross-linking strategy often improves the compactness of membranes which affects the migration speed of cations in the membrane phase,and it thus obtains an enhanced perm-selectivity.While it can be seen that high cross-linking would cause high electrical resistance that is not desirable for the practical ED application[30,31].

3.2.Surface modification

Surface modification is adopted to decrease the electrical resistance and maintain monovalent ion perm-selectivity simultaneously by tailoring the surface properties of the membranes.Unlike covalent crosslinking structure in membrane matrix,in this way,only the membrane surface is decorated by a functional layer,and it is thus expected to obtain high ionic flux and low electrical resistance.The modification techniques can be divided into two categories:surface physicochemical modification and covalently chemical modification.

3.2.1.Surface physicochemical modification

The physicochemical modification includes surface polymerization[32,33],direct coating[34,35],electrode position[36,37],and layer-bylayer self-assembly[14,25].Here,examples of the reported surface modified membranes have been taken to illustrate the versatility of the physicochemical modification.To produce a compact polymer layer by polymerizing monomerse.g.pyrrole,aniline and dopamine on the membrane surface is a very typical method among them.Such polymerization technique is facile and the polymer layer shows good adjust ability and affinity to the IEM matrix[16,38-40].The modified layer brings hydrophilic nature and different charge density from functional groups,which leads to adjusted surface compactness,contact angle,conductivity and perm-selectivity.For example,Gohilet al.[38]developed MPCMs with a polypyrrole layer.The dialysis rate decreased in the sequence of NaCl＞CaCl2＞MgCl2＞CuCl2and relative dialysis rates of NaCl with respect to different divalent electrolyte were varied between 5 and 8 in the use of mixed electrolytes,indicating the compact polypyrrole layer on the membrane surface could serve as a rejection layer for the migration of bulky ions,and the efficient separation of mono-/di-valent electrolyte was achieved.In fact,a compact layer on the membrane surface,no matter a polymer layer or an inorganic layer,is beneficial to strengthen the pore-size sieving effect and improve the perm-selectivity.Recently,a novel modification method through controllable metal loading on the surface of poly(2-acrylamido-2-methyl-propane-sulfonic acid)(PMPS)membranes by an electro-less plating technique was proposed by Thakuret al.(Fig.1)[41].The metal loading on the membrane surface could form a thin rigid layer,and it partially inhibited the ionic transport of bulkier cations.Due to the improved surface compactness,the flux ratio between Na+and Ni2+/Zn2+was significantly increased up to～100.The membranes exhibited excellent monovalent cation permselectivity without any significant deterioration in Na+transport.This work provides a new sight on fine tuning perm-selectivity and ionic flux of the CEM by constructing a thin metallic layer.

Fig.1.Preparation of the metal loaded PMPS membrane.(Reproduced from Ref.[41].)

In addition,Farrokhzadet al.[15]prepared PCMPs by decorating polyaniline(PANI)on sulfonated CEM surface with different doping agent.The dense PANIlayer had a lowercharge density than the pristine membrane and it hindered the migration of Mg2+ions through the membrane compared to Na+ions.In addition,the different hydrophilicity of the membrane surface caused by different doping agent would also affect the transport behaviors of the cations resulting from the different hydration energy of cations.The composite membrane coated by PANI-pTSA(para-toluene sulfonic acid)exhibited a very high selectivity for monovalent ions(～7.1).The hydrophilic surface actually facilitated the transport of Mg2+ions and the hydrophobic surface led to the easier diffusion of Na+ions,resulting from the energy barrier of partial ion dehydration[42,43].These results clearly reveal that the permselectivity is determined by the hydrated ionic size and the water affinity(the Gibbs hydration energy)of cations[44,45].

Rodzik[46]modified cation exchange membranes(CEMs)surface by two different methodsviz.electro depositing and coating aqueous chitosan hydrochloride,it was found that the introduction of chitosan layer boosted the perm-selectivity of the membranes obviously.A higher perm-selectivity of Na+over Mg2+could be observed by increasing the thickness of chitosan layerviaincreasing electrolyte concentration,applied current density and sorption time.Importantly,the authors claimed that apart from the pore-size sieving effect,the electrostatic barrier effect of the chitosan layer should also be taken into account in evaluation of membrane perm-selectivity.

In fact,some other studies also reported that multivalent cations were difficult to adsorb in anion exchange membranes(AEMs)as compared to monovalent cations,because of the difference in the electrostatic repulsion between the relevant cations and the membranes[47].In view of this,Amara and Kerdjoudj[48]prepared MCPMs by immersion and electrodeposition methods to adsorb highly protonated polyethyleneimine(PEI),the perm-selectivity of the membrane increased due to the strong repulsion effects of protonated PEI multilayers to divalent ions.Notably,PEI here was an effective carrier for protonviathe acid-base reaction between ammonium and amine groups,which facilitated the transport of H+ions and thus improved the permselectivity of H+/metallic ions.Huet al.[49]reported that electrodepositing quaternized chitosan layer improved the monovalent ion selectivity of the base membrane.After the formation of quaternized chitosan layer,Zn2+leakage dropped abruptly from 9.36%to 1.035%and Al3+leakage declined from 7.75%to 0.83%,which could be attributed to the electrostatic repulsion between metallic ions and cationic layer during the selective separation process of H+ions from multivalent cations.In summary,positively charged ion exchange groups are desirable to the CEMs in order to permeate preferentially monovalentcations rather than multivalentcations.However,it is noted that the electrodeposition or immersion method leads to monolayer adsorption of polyelectrolyte,the improvement of the perm-selectivity is still limited.

地域文化是由多个文化群体所构成的文化空间区域，区域的地理环境、人们的生产方式、社会生活方式和历史文化传统决定了地域文化的特征[6]7。地域文化景观是地域文化的载体，保存了区域内大量物质形态的历史景观和非物质形态的传统习俗[7]91，具有重要的历史、文化和观赏价值。地域文化的保护与挖掘对旅游业的发展十分重要，因为地域文化差异是激发游客旅游动机的主要因素之一[8]127。这一主题在地域文化与旅游开发领域已有不少研究，包括地域文化景观研究[9]、地域文化空间研究[10]、地域文化与旅游规划[11]以及文化旅游空间分析[12]等。

Recently,a layer-by-layer(LBL)polyelectrolyte deposition method is employed to enhance the perm-selectivity of IEMs by producing ultrathin coating on the membrane surface,an ultrathin multilayer could be achieved by an alternating adsorption of polycations and polyanions[14,17,50-53].The high charge density may induce the enhanced electrostatic interaction and size-based exclusion of highly hydrated ions,and it thereby improves the perm-selectivity of the membranes.For example,Chenget al.applied LBL technique to prepare 5-bilayer poly(sodium 4-styrene sulfonate)(PSS)and protonated poly(allylamine hydrochloride)(PAH) films on a nanofiltration membrane or porous alumina membrane,the selectivity for K+/Mg2+could be as high as～100.However,the uncharged membrane substrates caused low transference numbers of the LBL modified membranes,which limited theirutility in ED process that required transportofonly cations oranions through a membrane[54].To eliminate these defects,positively charged Na fion 115 membrane was used as a substrate for the preparation of MCPMs by LBL technique.Remarkably,the K+/Mg2+selectivity values were more than 1000 as the current density was at or below 1.59 mA·cm-2(Fig.2)[24].The high perm-selectivity was actually originated from the large hydrated ionic radius and electrostatic repulsion force of multivalent ions[18].These findings are expected to direct the design of MCPMs for mono-/multi-valentcation separation in ED process.

Fig.2.Coating of CEM with a polyelectrolyte multilayer to achieve high K+/Mg2+perm-selectivity.(Reproduced from Ref.[24].)

To date,the perm-selective ion separation of LBL modified membranes still remains a big challenge.A detailed and deep description of ion transport through the multilayer architectures is needed as the results from different studies are controversial[14].In fact,parameters in LBL process such as the number of layers,thickness,compartment concentration,applied current density and boundary layer thickness play important roles in the final performance[18,24,25,54,55].For example,when PEI/PSS multilayers as a perm-selective layer were coated on a Neosepta CMX membrane by LBL method,all the PEI/PSS modified membranes showed higher limited current density of approximately～20 mA·cm-2than that of PAH/PSS modified Nafion membranes[24,25],but,the Na+/Ca2+perm-selectivity was only 1.35,which was not so attractive.

Furthermore,the relatively weak physical interactions between ionic polyelectrolyte and ion exchange groups of the membrane would induce gradual decrease of perm-selectivity during a continuous operation process[56,57].In conclusion,systematic researches on diversified parameters in LBL process should be considered to investigate the mechanism on how the parameters affect the final performance of the membranes.

3.2.2.Surface chemical modification

As mentioned above,the long-term stability of modified layer of membranes in ED process still remains unsatisfactory.In these techniques,they only involve the physical interactions such as electrostatic attraction and intermolecular force between the modified layer and membrane matrix.In order to overcome this drawback,other approaches such as diazonium-induced anchoring process[58,59],photo-induced covalent immobilization[60]and the formation of a sulfonamide bond[61-63]have been proposed to form a stable connection between membrane matrix and the modified layer.For example,Chamoulaud and Belanger[64]converted sulfonic acid groups of a base membrane into--SO2Cl groups which subsequently reacted with a diamine to create a sulfonamide bond and a tertiary amine terminal,and finally incorporated with methyl iodide or protonation to obtain a cationic layer on the membrane surface(Fig.3).The ED results demonstrated a significant decrease in Zn2+leakage from 6.8%to 0.3%because the cationic layer allowed the transport of H+ions,but blocked the Zn2+ions due to the electrostatic barrier.Liet al.[65]decorated chlorosulfonated groups on membrane surface to react with polyquaternium-7.Due to the electrostatic exclusion from the modified thin layer,an obvious decrease in the metal ions leakage(Zn2+leakage decreased from 22.0%to 14.2%,Ca2+leakage from 53.1%to 38.0%and Mg2+leakage from 81.7%to 32.8%)could be observed.In addition,Ca2+and Mg2+have the equal electrostatic force,the different final perm-selectivity of Ca2+/Mg2+ions suggested that the steric barrier played a more important role in perm-selectivity.However,these membranes exhibited good monovalent cation perm-selectivity and durability,and hazardous chemicals such as SOCl2were used to prepare--SO2Clgroups.Therefore a more effective diazonium-induced anchoring process(DIAP)was proposed by Leet al.[66],in which a thin“polyaniline-like”layer was inserted covalently on the surface of commercial CMV membrane through a one-step chemical process(Fig.4).Compared with the pristine membrane,a great enhancement in perm-selectivity from 17.9 to 166.7 between H+ions and Ni2+ions was achieved.Most interestingly,the membrane resistance increased very slightly(about 8%)as the modified layer by DIAP was very thin.In another similar work[58],diazonium-induced carboxyl groups were grafted on the membrane surface by covalent immobilization of PEI multilayer.The divalent cation leakage of the modified membranes was decreased remarkably(Mg2+leakage from 7.1%to 0.4%and Zn2+leakage from 2.1%to 0.55%)which was ascribed to the electrostatic force of repulsion between the cations and the attached positively charged PEI multilayer.Thus,this method shows superior advantages to other available chemical modification methods[53,56,60].

3.3.Polymer blending

Fig.3.Modification of the CEM by chlorosulfonation(Reaction 1),amination(Reaction 2),and quaternization(Reaction 3).(Reproduced from Ref.[64].)

Fig.4.Modification of CMV by DIAP:(1)diazotization,(2)reduction of the aryldiazonium groups,(3)grafting of the aryl radicals onto the surface,and(4)growing of PAP multilayer.(Reproduced from Ref.[66].)

As previously stated,the perm-selectivity is not only determined by the pore-size sieving effect and electrostatic repulsion,but also influenced by the Gibbs hydration energy of cations.Thus,it is available to tune the hydrophobicity and hydrophilicity of membranes to improve the perm-selectivity.Polymerblending is a very usefultechnique to fabricate MCPMs which combines the hydrophilic and hydrophobic characterizations of different polymers into a polymer hybrid,and thus improves the resulting stability,perm-selectivity and conductivity[67].In such polymer hybrid,the hydrophilic polymer partcreates plenty of constructed water channels which facilitate ion transport,meanwhile the hydrophobic polymer part can restrict the water swelling,as a result,improved perm-selectivity of IEMs can be obtained.The perm-selectivity is controlled by the different migration speed of the respective ions and affinity of the ions with the membrane[12,44].A good modification procedure should balance the hydrophobicity and hydrophilicity of membranes because too many hydrophilic groups would cause perm-selective failure.Some studies tried to adjust the ratio of hydrophobic/hydrophilic groups in the membranes to optimize the interaction between ions and membrane matrix.For example,Balsteret al.[68]prepared MCPMs by blending hydrophilic sulfonated poly(ether ether ketone)(SPEEK)and hydrophobic poly(ether sulfone)(PES),the Ca2+transport through the membrane was actually determined by the conductivity and the charge density of the membrane.In addition,blending of SPEEK with poly(arylene etherketone)derivatives containing crown ether(CPAEK)induced significant increase of the K+over Li+selectivity by a factor of nearly 4 due to the tuned hydrophobicity of the blend membranes and the complexation interaction between K+and the crown ether.It is believed that polymer blending is a versatile method either to tune the hydrophobicity and hydrophilicity of the blend membranes or introduce the specific complexing-forming groups in the membranes,which further adjusts the final ionic flux and permselectivity[69].Moreover,simplicity is an obvious advantage of this method.However,to achieve a significantly improved permselectivity still remains a big challenge due to the limited inherent properties of the used polymers.

4.Emerging Technologies for Manufacturing MCPMs

4.1.Electro-spinning for constructing ionic channels

Electrospinning technique is an emerging technology for preparing polymeric fibers which can be used in the membrane preparation by further compressing procedure.For example,nano fibrous composite membranes were obtained by electrospinning quaternized poly(2,6-dimethyl-1,4-phenyleneoxide)/silicon dioxide hybrid material(QPPO-SiO2)followed by solvent fumigation and hot-press[70].The resulting membranes possessed interconnected porous structure,large specific surface area and good flexibility to offer an ion conductive pathway,and exhibited desirable transport properties and enhanced structural stability.Both acid permeability(UH=0.053 m·h-1)and selectivity(S=68.1)of the nano fiber composite membranes increased as compared to solution-cast QPPO-SiO2membrane(UH=0.041 m·h-1andS=49.5)for acid recovery during diffusion dialysis process.Chakrabartyet al.also reported the fabrication of electro-spun nanofibrous membranes composed of SPEEK for selective electrotransport of ions.The nanofibrous membranes exhibited very low flux and electro-transport efficiency of divalent cations,which showed a promise to purify brackish water into potable drinking water in the chloralkali industry[71].Recently,our group developed a new method to tailornano fibrous composite membranes containing--N+(CH3)3and--SO3-groups by impregnating QPPO nanofibrous mats into sulfonated poly(2,6-dimethyl-1,4-phenylene oxide)(SPPO)solution.Sulfonic groups of SPPO acted as continuous carriers for cations transmission while the quaternary ammonium groups played an important role in separating monovalent cations from divalent cations according to the electrostatic repulsion.As shown in Fig.5,compared with the commercial monovalentcation selective membrane(CSO),the optimized membrane exhibited higher ionic flux of2.96 × 10-8mol·cm-2·s-1and the perm-selectivity of 1.62.Meanwhile,the unique structure resulted in lower electrical resistance,higher limited current density and significant improvement in dimensional stability[72].

4.2.Nanofiltration alike membrane for electrodialysis(EDNF)

Traditionally,ion exchange membranes prepared by solvent evaporation method are dense ones.The dense structure limits the ion diffusion,ionic flux and high surface resistance as well.On the contrary,nano filtration membranes and ultra filtration membranes prepared by phase inversion technique are typically porous and they have relatively high flux.Therefore,it is reasonable to construct porous structures in ion exchange membranes would be expected to get high ionic flux and low surface resistance.Klaysomet al.prepared porous cation exchange membranes by blending sulfonated SiO2mesoporous silica with sulfonated polyethersulfoneviaphase inversion technique.The porosity and pore size of the ion exchange membranes increased with increasing SiO2loading and thus significantly enhanced ionic conductivity and transport properties.The optimal membrane had a high transport number of 0.95 as well as good mechanical strength and thermal stability.Electrodialysis experiments showed that both the current efficiency and the energy efficiency could be comparable with the commercial ion exchange membrane.Sunet al.[73]used porous BPPO-based AEMs for acid recoveryviadiffusion dialysis.The porous morphology of the membrane conduced the decreasing ion transport resistance.The proton dialysis coefficients were in the range of 0.020 to 0.025 m·h-1at 25 °C,whereas the separation factors appeared from 28.6 to 45.5.Both were higher than those of commercial dense DF-120 AEM(0.009 m·h-1and 18).A similar work was conducted by our group in which charged porous membranes with tunable morphologies were preparedviaNIPS technique foracid recovery.It could be seen that the finger-like structure provided higher dialysis coefficient of H+but lower selectivity,while the sponge-like structure displayed outstanding H+dialysis coefficients and separation factors.Specifically to the HCl/AlCl3system,the separation factor reached as high as 2033[74].Inspired by these successful applications and excellent performances of porous ion exchange membranes in ED and DD process,it stands to reason that whether or not the porous membranes can conduce good performances for monovalent cation perm-selectivity separation.

Fig.5.Schematic transport of Na+,Mg2+through the nanofibrous composite membrane.

Generally,a nanofiltration membrane has a porous bulk structure and a dense layer,the monovalentions could pass through but the multivalentions are blocked up under the pressure drop.While electrodialysis can allow the ion transport according to the charge,e.g.anions move towards anode through an AEM andvice versafor cations.Hence can we combine them into one membrane unit?i.e.,can we use a nanofiltration-like membrane to separate selectively mono-/multivalent ionsviaelectrodialysis?To verify this thinking,a nanofiltration like membrane was prepared by non-solvent induced phase separation and interfacial polymerization and integrated with ED process for selective ion separation.As shown in Fig.6A,in this process,the ions transfer through the nanofiltration-like membrane from one side to other side under an electric field,which can realize the concentration and desalination of the solution.The dense layer of nanofiltration-like membrane rejects the multivalent cations rather than the monovalent cations due to the different hydrated ionic radii of ions,leading to a high permselectivity of Na+and Mg2+ions.Furthermore,the porous structure of nanofiltration-like membrane can largely decrease the transfer resistance of ions and enhance the flux of monovalent ions.As a result,the H+ion flux could reach to 3.4 × 10-7mol·cm-2·s-1with the ion flux ratio of 354 for H+/Zn2+system(Fig.6B)and achieve 2.2 × 10-7mol·cm-2·s-1ofNa+ion flux with the ion flux ratio of7 for Na+/Mg2+system(Fig.6C)in this new process.Both of the permselectivity and ionic flux were higher than those of CSO membrane[26].The results clearly demonstrate the superiority of EDNF process in which effective separation of monovalent cations from divalent cations and desalination and concentration of solution are achieved simultaneously.

4.3.Mixed matrix membranes(MMMs)by organic-inorganic hybrid

Mixed matrix membranes(MMMs)comprised of polymeric components and embedded inorganic particles are promising for designing high performance IEMs[75-77].MMMs combine the advantages of both polymers(e.g.flexibility,adjustable IEC and processing ability)and inorganic particles(e.g.ion adsorption ability,thermal and mechanical stability).Generally,multi-phase MMMs can be prepared to manifest the desired properties of each component.In order to improve the monovalent ion perm-selectivity of IEMs,many inorganic particles(e.g.SiO2nanoparticles[78],multi-walled carbon nanotubes[79],iron-nickel oxide nanoparticles[80]and Fe3O4/PAA core-shell nanoparticles[81])are employed to cooperate into the polymer matrix.For example,Hosseiniet al.[82]prepared polyvinylchloride-co-TiO2nanoparticle MMMs by solution casting technique.The prepared MMMs had a different transport behavior for Na+ions and Ba2+owing to the different TiO2nanoparticle loading ratio.When the ions transferred across the MMMs,the ionic flux was affected by many factors including the adsorption ability of TiO2,the formation of narrow channels by TiO2as well as the decreased resin particles' accessibilityviaan isolating phenomenon.The iron-nickel oxide(Fe2NiO4)nanoparticle was also used to fabricate MMMs for ion separation[80].Interestingly,due to the good adsorption property of Fe2NiO4to Ba2+ions,the ionic permeability and flux of Ba2+ions increased with the increasing Fe2NiO4content,the MMMs showed higher perm-selectivity for divalent cations compared to monovalent cations.Apart from the above-mentioned works,our group proposed a graphene oxide(GO)embedded “three-phase”membrane composed of hydrophilic phase,hydrophobic phase and auxiliary phase(Fig.7).For the auxiliary phase,the formation of hydrogen-bonding networks and the increase of the hydrophilicity led to more efficient transfer of H+ions.Meanwhile,the strong adhesive force between Fe2+ions and the oxygen-containing groups attached on the GO sheets' surfaces hindered the transport of Fe2+.As a result,both acid permeability(UH=0.029 m·h-1)and selectivity(S=115)of the “three-phase”membranes increased as compared to “twophase”membrane(UH=0.021 m·h-1andS=76)for acid recoveryviadiffusion dialysis,indicating the introduction of added auxiliary phase successful beat the “trade-off”effect[83].

In general,the study of MMMs for ion separation is still at an infancy stage,more investigations should be carried out including the effect of the adsorption characterization,the size and dimensions,the shapes(layered,porous,and compact structures),and the dispersion of particles in polymer matrices on the ionic flux and perm-selectivity.

Fig.7.Schematic procedure to synthesize the “three-phase”AEMs containing GO sheets.

4.4.Other technologies

Besides the above-mentioned technologies,some other technologies are available to endow the IEM perm-selectivity.As mentioned above,the additional cross-linking agents are adopted in some researches to improve the compactness of the membranes.However,for semicrystalline polymeric ion exchange membrane,the annealing post treatment is an alternative way of operating the crystallization process and thus improving the selectivity in various applications including gas separation[84],vapor permeation[85]and ion-selective permeation[86,87].Our group proposed an annealing procedure to adjust crystallinity and enhance crystalline domains in polyvinyl alcohol based CEM,the as-obtained CEM exhibited improved pore-size sieving effect of ions.The larger Stokes radii of Zn2+ions were much more difficult to transport through the dense membrane than the smaller H+.The annealed membrane with a crystallinity of 43.9%exhibited a favorable perm-selectivity of142.9 between H+and Zn2+and extremely low Zn2+leakage of 0.01%[88].Alternatively,constructing ion channelsviaacid-base interaction has been done by many researches in fuel cell membranes,which can also significantly improve the compactness of a membrane matrix[89-93].In one of our works,we successfully constructed MCPMs through the formation of acid-base pairs of imidazole and sulfonic acid groups(Fig.8).The hydrogen bonding networks integrated with the acid-base pairs enabled the denser membrane structure,which lowered the Zn2+leakage compared with the pristine membrane.More importantly,this method induced micro-phase separation in membranes and the hydrophilic acid-based pair regions became inter-connected with each other(Fig.9),offering more conducting channels for the transportation ofH+.As a result,it achieved a high perm-selectivity of 333.3 between H+and Zn2+and extremely low Zn2+leakage of 0.05%.Apparently,the improvement in membrane compactnessviathis approach blocked the Zn2+transportation and increased the perm-selectivity of H+significantly.Due to the phaseseparation,the membrane area resistance was lower than that of the pristine SPPO membrane in acid solution,it was another advantage of this method[94].It is suggested that the acid-base interaction can be considered as a promising way of preparing MCPMs by controlling the area resistance or perm-selectivity.

5.Summary and Perspective

Fig.8.Constructing H+transfer channels in the membranes through the formation of acid-base pairs.

MCPMs especially possessing monovalent cation perm-selectivity have emerged as new type of IEMs which serve as the core components in traditional industries and innovative energy technologies.Since few decades,MCPMs have shown lots of potential applications such as production of sodium chloride[95],acid recovery in hydrometallurgy[61],removal of specific ions in liquid waste[18,96,97],lithium recovery from brine[8]and reverse electrodialysis for blue energy[5,98]benefiting from their high monovalent ion perm-selectivity compared to unmodified polymeric membranes.Although the current progress in exploring MPCMs is prominent,still there remain plenty of challenges,more detailed and systematic studies have to be made.For example,the limited current density should be promoted to ensure the high perm-selectivity in practical ED applications[24].In addition,the“trade-off”effect between ionic flux and perm-selectivity is a big issue in fabrication of high-performance MCPMs as clearly presented in Fig.10.It is clearly shown that the system of H+and metallic ions is the easiestone to separate as compared to the other systems.Especially,the values of ionic flux and perm-selectivity of nanofiltration alike membrane for H+/Zn2+system lie in the attractive region,indicating the advantage of porous membrane for ion separation.Furthermore,constructing ion channels and introducing the auxiliary phase can be considered as promising ways of beating the “trade-off”effect.For K+/Mg2+,Na+/Mg2+and Na+/Ca2+systems,which existed extensively in seawater,the ionic flux and perm-selectivity still remain unsatisfactory,either a low perm-selectivity with high ionic flux or a high permselectivity with low ionic flux.In a word,how to beat the “trade-off”effect and to get high-performance MCMPs with high perm-selectivity and ionic flux is a challenge that needs urgent solutions.

Fig.9.AFM phase images of SPPO(left)and acid-base pair(right)membranes.

Fig.10.Upper bound relationship for monovalent cation and multi-valent cation separation.Data collected from Refs.[15,16,24-26,38,41,42,54,99-101].

Generally,mono-/multi-valent cation separation depends on the pore-size sieving effect,the different Gibbs hydration energy of cations and the electrostatic repulsive forces,which are governed essentially by the affinity with the membrane and the relative migration speed in the membrane phase.Apart from the intrinsic characteristics of materials,choosing appropriate preparation methods is of pivotal importance to endow the perm-selective permeability to the traditional IEMs.Currently,a series of approaches such as covalent cross-linking,surface modification,polymer blending,electrospinning,fabricating nanofiltration-like membrane,organic-inorganic hybrid and other technologies have been proposed,the prepared membranes show enhanced perm-selectivity by adjusting the affinity of the cations with membrane and their migration speed in the membrane phase.Each technique has their own advantages and limitation.For example,covalent cross-linking and annealing technologies can improve the compactness of the membranes and thus lead to an increase in perm-selectivity.However,it brings the high electrical resistance of the membranes.Surface modification technology is expected to obtain high ionic flux and low electrical resistance,but the long-term stability of modified layer or the complicated producing process still remains unsatisfactory.Simplicity is a big advantage for polymer blending and organic-inorganic hybrid technologies,nevertheless,a significantly improved permselectivity is unable to be achieved due to the limitation on the inherent properties of the used components.Some emerging technologies,such as electrospinning,constructing ion channels and introducing porous structure in the membranes,could prepare MCMPs with preferable properties.Further researches should be considered to investigate the mechanisms of the perm-selective process in MCMPs and how the specific parameters affect the performances.

In addition,available ion separation mechanisms should be proposed by means of deep understanding towards the ion transportissues within a confined space of ionic channels[102].MPCMs in the use of functional porous materials such as polymers of intrinsic micro-porosity(PIM),Troger's Base(TB),metal-organic frameworks(MOFs)and covalent organic frameworks(COFs),are also gradually applied for ionic separation due to the controllable framework structure and pore size as well as ion exchange/adsorption ability.Furthermore,layered dimensional materials with unique atomic thickness and micrometer lateral dimensions,such as zeolite[103],graphene oxide[21,104]and 2D MoS2nanosheets[105]have been explored increasingly as fundamental platforms to develop ion transport and separation technologies[106].Finally,these new materials and manufacturing methods would endow the membranes with excellent monovalent cation permselectivity,considerable monovalent cation flux,low electrical resistance,high limited current density and long-term stability.

[1]M.Elimelech,W.A.Phillip,The future of seawater desalination:energy,technology,and the environment,Science333(2011)712-717.

[2]A.Oehmen,D.Vergel,J.Fradinho,M.A.Reis,J.G.Crespo,S.Velizarov,Mercury removal from water streams through the ion exchange membrane bioreactor concept,J.Hazard.Mater.264(2014)65-70.

[3]A.Mahmoud,A.F.Hoadley,An evaluation of a hybrid ion exchange electrodialysis process in the recovery of heavy metals from simulated dilute industrial wastewater,Water Res.46(2012)3364-3376.

[4]J.W.Post,Blue Energy:Electricity Production From Salinity Gradients by Reverse Electrodialysis,Wageningen Universiteit,2009.

[5]M.Reig,H.Farrokhzad,B.van der Bruggen,O.Gibert,J.L.Cortina,Synthesis of a monovalent selective cation exchange membrane to concentrate reverse osmosis brines by electrodialysis,Desalination375(2015)1-9.

[6]F.D.R.Amado,M.A.S.Rodrigues,F.D.P.Morisso,A.M.Bernardes,J.Z.Ferreira,C.A.Ferreira,High-impact polystyrene/polyaniline membranes for acid solution treatmentby electrodialysis:Preparation,evaluation,and chemical calculation,J.Colloid Interface Sci.320(2008)52-61.

[7]J.Lambert,M.Avila-Rodriguez,G.Durand,M.Rakib,Separation of sodium ions from trivalent chromium by electrodialysis using monovalent cation selective membranes,J.Membr.Sci.280(2006)219-225.

[8]Z.Y.Ji,Q.B.Chen,J.S.Yuan,J.Liu,Y.Y.Zhao,W.X.Feng,Preliminary study on recovering lithium from high Mg2+/Li+ratio brines by electrodialysis,Sep.Purif.Technol.172(2017)168-177.

[9]X.-Y.Nie,S.-Y.Sun,Z.Sun,X.Song,J.-G.Yu,Ion-fractionation of lithium ions from magnesium ions by electrodialysis using monovalent selective ion-exchange membranes,Desalination403(2017)128-135.

[10]M.C.Martí-Calatayud,D.C.Buzzi,M.García-Gabaldón,A.M.Bernardes,J.A.S.Tenório,V.Pérez-Herranz,Ion transport through homogeneous and heterogeneous ion-exchange membranes in single salt and multicomponent electrolyte solutions,J.Membr.Sci.466(2014)45-57.

[11]T.Sata,Studies on ion exchange membranes with permselectivity for specific ions in electrodialysis,J.Membr.Sci.93(1994)117-135.

[12]T.Sata,W.K.Yang,Studies on cation-exchange membranes having permselectivity between cations in electrodialysis,J.Membr.Sci.206(2002)31-60.

[13]M.Wang,C.Gao,The state-of-the-artofthe cation exchange membrane having monovalent ion selectivity—A patent review,Recent Pat.Chem.Eng.4(2011)132-140.

[14]R.Femmer,A.Mani,M.Wessling,Ion transport through electrolyte/polyelectrolyte multi-layers,Sci.Rep.5(2015)11583.

[15]H.Farrokhzad,M.R.Moghbeli,T.Van Gerven,B.van der Bruggen,Surface modification of composite ion exchange membranes by polyaniline,React.Funct.Polym.86(2015)161-167.

[16]H.Farrokhzad,S.Darvishmanesh,G.Genduso,T.van Gerven,B.van der Bruggen,Development of bivalentcation selective ion exchange membranes by varying molecular weight of polyaniline,Electrochim.Acta158(2015)64-72.

[17]S.Rajesh,Y.Yan,H.-C.Chang,H.Gao,W.A.Phillip,Mixed mosaic membranes prepared by layer-by-layer assembly for ionic separations,ACS Nano8(2014)12338-12345.

[18]N.White,M.Misovich,E.Alemayehu,A.Yaroshchuk,M.L.Yaroshchuk,Bruening,Highly selective separations of multivalent and monovalent cations in electrodialysis through Na fion membranes coated with polyelectrolyte multilayers,Polymer103(2016)478-485.

[19]J.Ran,L.Wu,Y.He,Z.Yang,Y.Wang,C.Jiang,L.Ge,E.Bakangura,T.Xu,Ion exchange membranes:new developments and applications,J.Membr.Sci.522(2017)267-291.

[20]T.-Y.Liu,H.-G.Yuan,Q.Li,Y.-H.Tang,Q.Zhang,W.Qian,B.van der Bruggen,X.Wang,Ion-responsive channels of zwitterion-carbon nanotube membrane for rapid water permeation and ultra-high mono-/multivalent ion selectivity,ACS Nano9(2015)7488-7496.

[21]R.Joshi,P.Carbone,F.Wang,V.Kravets,Y.Su,I.Grigorieva,H.Wu,A.Geim,R.Nair,Precise and ultrafast molecular sieving through graphene oxide membranes,Science343(2014)752-754.

[22]B.Mi,Graphene oxide membranes for ionic and molecular sieving,Science343(2014)740-742.

[23]A.M.Balachandra,J.Dai,M.L.Bruening,Enhancing the anion-transport selectivity of multilayer polyelectrolyte membranes by templating with Cu2+,Macromolecules35(2002)3171-3178.

[24]N.White,M.Misovich,A.Yaroshchuk,M.L.Bruening,Coating of na fion membranes with polyelectrolyte multilayers to achieve high monovalent/divalent cation electrodialysis selectivities,ACS Appl.Mater.Interfaces7(2015)6620-6628.

[25]S.Abdu,M.-C.Martí-Calatayud,J.E.Wong,M.García-Gabaldón,M.Wessling,Layerby-layer modification of cation exchange membranes controls ion selectivity and water splitting,ACS Appl.Mater.Interfaces6(2014)1843-1854.

[26]L.Ge,B.Wu,Q.Li,Y.Wang,D.Yu,L.Wu,J.Pan,J.Miao,T.Xu,Electrodialysis with nanofiltration membrane(EDNF)for high-efficiency cations fractionation,J.Membr.Sci.498(2016)192-200.

[27]Y.M.Onouc,R.Yamanc,Y.Takasaki,Permselectivity of improved cation exchange membranes for NaCl-CaCl2system,Denki Kagaku29(1961)544.

[28]T.Sata,Modification of properties of ion-exchange membranes.IV.Change of transport properties of cation-exchange membranes by various polyelectrolytes,J.Polym.Sci.Polym.Chem.Ed.16(1978)1063-1080.

[29]M.Kumar,B.P.Tripathi,V.K.Shahi,Ionic transport phenomenon across sol-gel derived organic-inorganic composite mono-valent cation selective membranes,J.Membr.Sci.340(2009)52-61.

[30]T.Sata,K.Teshima,T.Yamaguchi,Permselectivity between two anions in anion exchange membranes crosslinked with various diamines in electrodialysis,J.Polym.Sci.Part A Polym.Chem.34(1996)1475-1482.

[31]T.Sata,S.Nojima,Transport properties of anion exchange membranes prepared by the reaction of crosslinked membranes having chloromethyl groups with 4-vinylpyridine and trimethylamine,J.Polym.Sci.Part B Polym.Phys.37(1999)1773-1785.

[32]S.M.Hosseini,F.Jeddi,M.Nemati,S.S.Madaeni,A.R.Moghadassi,Electrodialysis heterogeneous anion exchange membrane modified by PANI/MWCNT composite nanoparticles:preparation,characterization and ionic transport property in desalination,Desalination341(2014)107-114.

[33]M.Kumar,M.A.Khan,Z.A.AlOthman,M.R.Siddiqui,Polyaniline modified organicinorganic hybrid cation-exchange membranes for the separation of monovalent and multivalent ions,Desalination325(2013)95-103.

[34]M.He,J.Yao,Q.Liu,K.Wang,F.Chen,H.Wang,Facile synthesis of zeolitic imidazolate framework-8 from a concentrated aqueous solution,Microporous Mesoporous Mater.184(2014)55-60.

[35]S.Ayala,Z.Zhang,S.M.Cohen,Hierarchical structure and porosity in UiO-66 polyMOFs,Chem.Commun.53(2017)3058-3061.

[36]R.Banerjee,A.Phan,B.Wang,C.Knobler,H.Furukawa,M.O'Keeffe,O.M.Yaghi,High-throughput synthesis of zeolitic imidazolate frameworks and application to CO2capture,Science319(2008)939-943.

[37]C.Chi,X.Wang,Y.Peng,Y.Qian,Z.Hu,J.Dong,D.Zhao,Facile preparation of graphene oxide membranes for gas separation,Chem.Mater.28(2016)2921-2927.

[38]G.S.Gohil,V.V.Binsu,V.K.Shahi,Preparation and characterization of mono-valent ion selective polypyrrole composite ion-exchange membranes,J.Membr.Sci.280(2006)210-218.

[39]M.Vaselbehagh,H.Karkhanechi,R.Takagi,H.Matsuyama,Surface modification of an anion exchange membrane to improve the selectivity for monovalent anions in electrodialysis—experimental verification of theoretical predictions,J.Membr.Sci.490(2015)301-310.

[40]M.Vaselbehagh,H.Karkhanechi,R.Takagi,H.Matsuyama,Effect of polydopamine coating and direct electric current application on anti-biofouling properties of anion exchange membranes in electrodialysis,J.Membr.Sci.515(2016)98-108.

[41]A.K.Thakur,M.Manohar,V.K.Shahi,Controlled metal loading on poly(2-acrylamido-2-methyl-propane-sulfonic acid)membranes by an ion-exchange process to improve electrodialytic separation performance for mono-/bi-valent ions,J.Mater.Chem.A3(2015)18279-18288.

[42]L.Firdaous,J.P.Malériat,J.P.Schlumpf,F.Quemeneur,Transfer of monovalent and divalentcations in saltsolutions by electrodialysis,Sep.Sci.Technol.42(2007)931-948.

[43]B.van der Bruggen,A.Koninckx,C.Vandecasteele,Separation of monovalent and divalent ions from aqueous solution by electrodialysis and nanofiltration,Water Res.38(2004)1347-1353.

[44]T.Sata,Studies on anion exchange membranes having permselectivity for specific anions in electrodialysis—effect of hydrophilicity of anion exchange membranes on permselectivity of anions,J.Membr.Sci.167(2000)1-31.

[45]T.Sata,Y.Yamane,K.Matsusaki,Preparation and properties of anion exchange membranes having pyridinium or pyridinium derivatives as anion exchange groups,J.Polym.Sci.Part A Polym.Chem.36(1998)49-58.

[46]I.Rodzik,Difference in transfer of magnesium and sodium ions through electrodialytic membranes modified with chitosan,Russ.J.Appl.Chem.81(2008)412-414.

[47]T.Xu,Ion exchange membranes:state of their development and perspective,J.Membr.Sci.263(2005)1-29.

[48]M.Amara,H.Kerdjoudj,Modified membranes applied to metallic ion separation and mineral acid concentration by electrodialysis,Sep.Purif.Technol.29(2002)79-87.

[49]Y.Hu,M.Wang,D.Wang,X.L.Gao,C.J.Gao,Feasibility study on surface modification of cation exchange membranes by quaternized chitosan for improving its selectivity,J.Membr.Sci.319(2008)5-9.

[50]S.Mulyati,R.Takagi,A.Fujii,Y.Ohmukai,H.Matsuyama,Simultaneous improvement of the monovalent anion selectivity and antifouling properties of an anion exchange membrane in an electrodialysis process,using polyelectrolyte multilayer deposition,J.Membr.Sci.431(2013)113-120.

[51]J.A.Armstrong,E.E.L.Bernal,A.Yaroshchuk,M.L.Bruening,Separation of ions using polyelectrolyte-modified nanoporous track-etched membranes,Langmuir29(2013)10287-10296.

[52]C.Sheng,S.Wijeratne,C.Cheng,G.L.Baker,M.L.Bruening,Facilitated ion transport through polyelectrolyte multilayer films containing metal-binding ligands,J.Membr.Sci.459(2014)169-176.

[53]Y.Zhao,K.Tang,H.Liu,B.van der Bruggen,A.Sotto Díaz,J.Shen,C.Gao,An anion exchange membrane modified by alternate electro-deposition layers with enhanced monovalent selectivity,J.Membr.Sci.520(2016)262-271.

[54]C.Cheng,N.White,H.Shi,M.Robson,M.L.Bruening,Cation separations in electrodialysis through membranes coated with polyelectrolyte multilayers,Polymer55(2014)1397-1403.

[55]N.White,Electrically driven ion separations and nanofiltration through membranes coated with polyelectrolyte multilayers,Ph.D.Thesis,Michigan State University,United States,2015.

[56]M.Wang,X.Liu,Y.-x.Jia,X.-l.Wang,The improvement of comprehensive transport properties to heterogeneous cation exchange membrane by the covalent immobilization of polyethyleneimine,Sep.Purif.Technol.140(2015)69-76.

[57]T.T.Yao,M.Wang,Y.X.Jia,P.F.Zhou,A modified coating method for preparing a mono-valent perm-selective cation exchange membrane:I.The evolution of membrane property corresponding to different preparing stages,Desalin.Water Treat.51(2013)2740-2748.

[58]X.Liu,M.Wang,Y.-x.Jia,Surface-functionalized cation exchange membrane by covalent immobilization of polyelectrolyte multilayer for effective separation of mono-and multivalent cations,Sep.Sci.Technol.(2016)1-10.

[59]X.Wang,M.Wang,Y.Jia,B.Wang,Surface Modification of Anion Exchange Membrane by Covalent Grafting for Imparting Permselectivity between Specific Anions,Electrochim.Acta174(2015)1113-1121.

[60]M.Wang,Y.X.Jia,T.T.Yao,K.K.Wang,The endowment of monovalentselectivity to cation exchange membrane by photo-induced covalent immobilization and selfcrosslinking of chitosan,J.Membr.Sci.442(2013)39-47.

[61]G.Chamoulaud,D.Belanger,Modification of ion-exchange membrane used for separation of protons and metallic cations and characterization of the membrane by current-voltage curves,J.Colloid Interface Sci.281(2005)179-187.

[62]K.Takata,Y.Yamamoto,T.Sata,Modification of transport properties of ion exchange membranes:14.Effect of molecular weight of polyethyleneimine bonded to the surface of cation exchange membranes by acid-amide bonding on electrochemical properties of the membranes,J.Membr.Sci.179(2000)101-107.

[63]K.Takata,Y.Yamamoto,T.Sata,Modification of transport properties of ion exchange membranes.15.Preparation and properties of cation exchange membranes having a single cationic charged layer on the membrane surface by sulfonyl-amide bonding,Bull.Chem.Soc.Jpn.69(1996)797-804.

[64]G.Chamoulaud,D.Belanger,Chemical modification of the surface of a sulfonated membrane by formation of a sulfonamide bond,Langmuir20(2004)4989-4995.

[65]J.Li,M.L.Zhou,J.Y.Lin,W.Y.Ye,Y.Q.Xu,J.N.Shen,C.J.Gao,B.V.D.Bruggen,Monovalent cation selective membranes for electrodialysis by introducing polyquaternium-7 in a commercial cation exchange membrane,J.Membr.Sci.486(2015)89-96.

[66]X.T.Le,P.Viel,P.Jegou,A.Garcia,T.Berthelot,T.H.Bui,S.Palacin,Diazoniuminduced anchoring process:An application to improve the monovalent selectivity of cation exchange membranes,J.Mater.Chem.20(2010)3750-3757.

[67]G.S.Gohil,R.K.Nagarale,V.V.Binsu,V.K.Shahi,Preparation and characterization of monovalent cation selective sulfonated poly(ether ether ketone)and poly(ether sulfone)composite membranes,J.Colloid Interface Sci.298(2006)845-853.

[68]J.Balster,O.Krupenko,I.Punt,D.F.Stamatialis,M.Wessling,Preparation and characterisation of monovalent ion selective cation exchange membranes based on sulphonated poly(ether ether ketone),J.Membr.Sci.263(2005)137-145.

[69]S.Tas,B.Zoetebier,M.A.Hempenius,G.J.Vancso,K.Nijmeijer,Monovalent cation selective crown ether containing poly(arylene ether ketone)/SPEEK blend membranes,RSC Adv.6(2016)55635-55642.

[70]J.Pan,Y.He,L.Wu,C.Jiang,B.Wu,A.N.Mondal,C.Cheng,T.Xu,Anion exchange membranes from hot-pressed electrospun QPPO-SiO2hybrid nano fibers for acid recovery,J.Membr.Sci.480(2015)115-121.

[71]T.Chakrabarty,M.Kumar,K.Rajesh,V.K.Shahi,T.Natarajan,Nano- fibrous sulfonated poly(ether ether ketone)membrane for selective electro-transport of ions,Sep.Purif.Technol.75(2010)174-182.

[72]L.Hou,J.Pan,D.Yu,B.Wu,A.N.Mondal,Q.Li,L.Ge,T.Xu,Nano fibrous composite membranes(NFCMs)for mono/divalent cations separation,J.Membr.Sci.528(2017)243-250.

[73]F.Sun,C.Wu,Y.Wu,T.Xu,Porous BPPO-based membranes modified by multisilicon copolymer for application in diffusion dialysis,J.Membr.Sci.450(2014)103-110.

[74]L.Ge,A.N.Mondal,X.Liu,B.Wu,D.Yu,Q.Li,J.Miao,Q.Ge,T.Xu,Advanced charged porous membranes with ultrahigh selectivity and permeability for acid recovery,J.Membr.Sci.536(2017)11-18.

[75]E.Bakangura,L.Wu,L.Ge,Z.Yang,T.Xu,Mixed matrix proton exchange membranes for fuel cells:State of the art and perspectives,Prog.Polym.Sci.57(2016)103-152.

[76]Q.Xin,T.Liu,Z.Li,S.Wang,Y.Li,Z.Li,J.Ouyang,Z.Jiang,H.Wu,Mixed matrix membranes composed of sulfonated poly(ether ether ketone)and a sulfonated metal-organic framework for gas separation,J.Membr.Sci.488(2015)67-78.

[77]B.Wu,L.Ge,D.Yu,L.Hou,Q.Li,Z.Yang,T.Xu,Cationic metal-organic framework porous membranes with high hydroxide conductivity and alkaline resistance for fuel cells,J.Mater.Chem.A4(2016)14545-14549.

[78]S.Hosseini,Z.Ahmadi,M.Nemati,F.Parvizian,S.Madaeni,Electrodialysis heterogeneous ion exchange membranes modified by SiO2nanoparticles:fabrication and electrochemical characterization,Water Sci.Technol.73(2016)2074-2084.

[79]S.M.Hosseini,P.Koranian,A.Gholami,S.S.Madaeni,A.R.Moghadassi,P.Sakinejad,A.R.Khodabakhshi,Fabrication of mixed matrix heterogeneous ion exchange membrane by multiwalled carbon nanotubes:electrochemical characterization and transport properties of mono and bivalent cations,Desalination329(2013)62-67.

[80]S.M.Hosseini,S.S.Madaeni,A.R.Heidari,A.Amirimehr,Preparation and characterization of ion-selective polyvinyl chloride based heterogeneous cation exchange membrane modified by magnetic iron-nickel oxide nanoparticles,Desalination284(2012)191-199.

[81]M.Nemati,S.M.Hosseini,Fabrication and electrochemical property modification of mixed matrix heterogeneous cation exchange membranes filled with Fe3O4/PAA core-shell nanoparticles,Ionics22(2016)899-909.

[82]S.M.Hosseini,M.Nemati,F.Jeddi,E.Salehi,A.R.Khodabakhshi,S.S.Madaeni,Fabrication of mixed matrix heterogeneous cation exchange membrane modified by titanium dioxide nanoparticles:mono/bivalent ionic transport property in desalination,Desalination359(2015)167-175.

[83]J.Ran,M.Hu,D.Yu,Y.He,M.A.Shehzad,L.Wu,T.Xu,Graphene oxide embedded“three-phase”membrane to beat “trade-off”in acid recovery,J.Membr.Sci.520(2016)630-638.

[84]Q.Song,S.Nataraj,M.V.Roussenova,J.C.Tan,D.J.Hughes,W.Li,P.Bourgoin,M.A.Alam,A.K.Cheetham,S.A.Al-Muhtaseb,Zeolitic imidazolate framework(ZIF-8)based polymer nanocomposite membranes for gas separation,Energy Environ.Sci.5(2012)8359-8369.

[85]A.Mahmood,S.Bano,S.-G.Kim,K.-H.Lee,Water-methanol separation characteristics of annealed SA/PVA complex membranes,J.Membr.Sci.415-416(2012)360-367.

[86]B.Li,B.Wang,Z.Liu,G.Qing,Synthesis of nanoporous PVDF membranes by controllable crystallization for selective proton permeation,J.Membr.Sci.517(2016)111-120.

[87]S.Liang,G.Xu,Y.Jin,Z.Wu,Z.Cai,N.Zhao,Z.Wu,Annealing of supporting layer to develop nanofiltration membrane with high thermal stability and ion selectivity,J.Membr.Sci.476(2015)475-482.

[88]L.Ge,L.Wu,B.Wu,G.Wang,T.Xu,Preparation of monovalent cation selective membranes through annealing treatment,J.Membr.Sci.459(2014)217-222.

[89]D.Wu,T.Xu,L.Wu,Y.Wu,Hybrid acid-base polymer membranes prepared for application in fuel cells,J.Power Sources186(2009)286-292.

[90]J.Yang,Q.Li,J.O.Jensen,C.Pan,L.N.Cleemann,N.J.Bjerrum,R.He,Phosphoric acid doped imidazolium polysulfone membranes for high temperature proton exchange membrane fuel cells,J.Power Sources205(2012)114-121.

[91]J.Wang,J.Liao,L.Yang,S.Zhang,X.Huang,J.Ji,Highly compatible acid-base blend membranes based on sulfonated poly(ether ether ketone)and poly(ether ether ketone-alt-benzimidazole)for fuel cells application,J.Membr.Sci.415(2012)644-653.

[92]H.Wu,X.H.Shen,Y.Cao,Z.Li,Z.Y.Jiang,Composite proton conductive membranes composed of sulfonated poly(ether ether ketone)and phosphotungstic acidloaded imidazole microcapsules as acid reservoirs,J.Membr.Sci.451(2014)74-84.

[93]C.V.Mahajan,V.Ganesan,Influence of hydrogen bonding effects on methanol and water diffusivities in acid-base polymer blend membranes of sulfonated poly(ether ether ketone)and base tethered polysulfone,J.Phys.Chem.B117(2013)5315-5329.

[94]L.Ge,X.Liu,G.Wang,B.Wu,L.Wu,E.Bakangura,T.Xu,Preparation of proton selective membranes through constructing H+transfer channels by acid-base pairs,J.Membr.Sci.475(2015)273-280.

[95]W.Zhang,M.Miao,J.Pan,A.Sotto,J.Shen,C.Gao,B.V.der Bruggen,Separation of divalent ions from seawater concentrate to enhance the purity of coarse salt by electrodialysis with monovalent-selective membranes,Desalination411(2017)28-37.

[96]H.Deng,S.Zhao,Q.Meng,W.Zhang,B.Hu,A novel surface ion-imprinted cationexchange membrane for selective separation of copper ion,Ind.Eng.Chem.Res.53(2014)15230-15236.

[97]S.Chaudhury,A.Bhattacharyya,A.Goswami,Electrodriven ion transport through crown ether-Na fion composite membrane:enhanced selectivity of Cs+over Na+by ion gating at the surface,Ind.Eng.Chem.Res.53(2014)8804-8809.

[98]E.Güler,W.van Baak,M.Saakes,K.Nijmeijer,Monovalent-ion-selective membranes for reverse electrodialysis,J.Membr.Sci.455(2014)254-270.

[99]R.K.Nagarale,G.S.Gohil,V.K.Shahi,G.S.Trivedi,R.Rangarajan,Preparation and electrochemical characterization of cation-and anion-exchange/polyaniline composite membranes,J.Colloid Interface Sci.277(2004)162-171.

[100]A.Moghadassi,P.Koranian,S.Hosseini,M.Askari,S.Madaeni,Surface modification of heterogeneous cation exchange membrane through simultaneous using polymerization of PAA and multi walled carbon nano tubes,J.Ind.Eng.Chem.20(2014)2710-2718.

[101]A.Chapotot,G.Pourcelly,C.Gavach,Transport competition between monovalent and divalent cations through cation-exchange membranes.Exchange isotherms and kinetic concepts,J.Membr.Sci.96(1994)167-181.

[102]Q.Wen,D.Yan,F.Liu,M.Wang,Y.Ling,P.Wang,P.Kluth,D.Schauries,C.Trautmann,P.Apel,Highly selective ionic transport through subnanometer pores in polymer films,Adv.Funct.Mater.26(2016)5796-5803.

[103]M.Tsapatsis,2-dimensional zeolites,AICHE J.60(2014)2374-2381.

[104]P.Sun,R.Ma,H.Deng,Z.Song,Z.Zhen,K.Wang,T.Sasaki,Z.Xu,H.Zhu,Intrinsic high water/ion selectivity of graphene oxide lamellar membranes in concentration gradient-driven diffusion,Chem.Sci.7(2016)6988-6994.

[105]J.Feng,M.Graf,K.Liu,D.Ovchinnikov,D.Dumcenco,M.Heiranian,V.Nandigana,N.R.Aluru,A.Kis,A.Radenovic,Single-layer MoS2nanopores as nanopower generators,Nature536(2016)197-200.

[106]G.Liu,W.Jin,N.Xu,Two-dimensional-material membranes:a new family of high-performance separation membranes,Angew.Chem.Int.Ed.55(2016)13384-13397.