Fluorescence Behavior of Biphenyl Containing Side-Chain Liquid Crystalline Polyacetylene with Various Lengths of Spacers

2012-11-06YUZhenQiangZHANGXinLIZiChenCHENErQiangLAMJackyTANGBenZhong

物理化学学报 2012年7期
关键词:深圳大学侧链联苯

YU Zhen-Qiang ZHANG Xin LI Zi-Chen CHEN Er-Qiang,*LAM Jacky W.Y. TANG Ben-Zhong

(1Beijing National Laboratory for Molecular Sciences,Key Laboratory of Polymer Chemistry and Physics of the Ministry of Education,Department of Polymer Science and Engineering,College of Chemistry and Molecular Engineering,Peking University,Beijing 100871,P.R.China; 2School of Chemistry and Chemical Engineering and Shenzhen Key Laboratory of Functional Polymers,Shenzhen University,Shenzhen 518060,Guangdong Province,P.R.China;3Department of Chemistry,The Hong Kong University of Science&Technology,Kowloon,Hong Kong,P.R.China)

Fluorescence Behavior of Biphenyl Containing Side-Chain Liquid Crystalline Polyacetylene with Various Lengths of Spacers

YU Zhen-Qiang1,2,*ZHANG Xin1LI Zi-Chen1CHEN Er-Qiang1,*LAM Jacky W.Y.3TANG Ben-Zhong3

(1Beijing National Laboratory for Molecular Sciences,Key Laboratory of Polymer Chemistry and Physics of the Ministry of Education,Department of Polymer Science and Engineering,College of Chemistry and Molecular Engineering,Peking University,Beijing 100871,P.R.China;2School of Chemistry and Chemical Engineering and Shenzhen Key Laboratory of Functional Polymers,Shenzhen University,Shenzhen 518060,Guangdong Province,P.R.China;3Department of Chemistry,The Hong Kong University of Science&Technology,Kowloon,Hong Kong,P.R.China)

Steady state fluorescence and fluorescence decay of a series of monosubstituted biphenyl containing sidechain liquid crystalline polyacetylenes with different lengths of spacers were investigated.For comparison,a monomer was selected as a model compound.Steady state fluorescence spectra elucidated that the polymers and the monomer showed single fluorescence emission arising from the biphenyl group on the side chain.With decreasing the length of the spacer,the fluorescence intensity of the polymer decreased accordingly.The fluorescence decay showed that the decay of the monomer could be fitted to be a single-exponential decay,while that of the polymers should be fitted to be a triple-exponential decay,which may be originated from the local high concentration induced quenching and the rotational restriction of the side-chain biphenyl groups.Solvent effects illustrated that the interaction between the solvents and the biphenyl groups strengthened with increasing the polarity of the solvents.

Steady state fluorescence; Monosubstituted polyacetylene; Biphenyl; Fluorescence lifetime;Solvent effect

The discovery of electroluminescence of poly(p-phenylenevinylene)[1]in 1990 has aroused wide interest of the application of conjugated polymers in the field of light-emitting and optoelectronics[2-3].To develop advanced materials with high quantum yield and high performance,many efforts have been directed toward molecular design and materials processing.Polyacetylene is a prototypical conjugated polymer,which has been intensively studied for decades[4-5].Polyacetylene with an extremely low solubility does not exhibit efficient luminescence properties[6-7].To achieve desirable photochemical and photophysical properties,mono-or di-substituted polyacetylenes with the sidechain containing appropriate chromophores have been designed;and their photoluminescence and/or aggregation induced emission behaviors have been studied[8-12].Considering improving and controlling the properties of substituted poly-acetylenes,the following four factors should be taken into account[13]:the configuration and regularity of the main chain,the nature of the substituent,the steric interaction of the side chain,and the degree of the conjugation.Among them,the forth factor,i.e.,the conjugation length of main chain may play an important role. However,the side-chain structure and the mode of how the sidechains are linked to the polyacetylene backbone in fact can greatly affect the conjugation length.

The biphenyl moieties are often employed as a building block for the fabrication of various luminescent materials[14-15].Tang and his co-workers have synthesized a series of mono-and bisubstitutedbiphenylcontaining polyacetylenes[16-19],and have studied the samples′phase behaviors[20-22],light emitting behaviors[23-24],and aggregation behaviors in dilute solutions[25].Some of the samples are found to be highly luminescent.The biphenyl group is also a typical mesogenic core.Usually,it is terminally attached to the polyacetylene backbone through a flexible spacer[15-16,20].In this regard,the resultant polymer belongs to the familyofside-chainliquidcrystallinepolyacetylenes(SCLCPAs). In this paper,we intend to study the spacer length dependence of the genuine fluorescence property of a monosubstituted SCLCPA,namely,poly((m+2)-{[(4′-heptyloxy-4-biphenylyl) carbonyl]oxy}-1-alkylyne)(abbreviated as P-m,7,where m is the number of the methylene units of the spacer,and the number 7 represents the carbon number of the side-chain tail,see Scheme 1).The steady state and time-resolved fluorescence behavior of P-m,7 were studied in comparison with that of a monomer(M-3,7,see Scheme 1)used as a model compound.The solvent effect in various solvents with different polarities was also investigated toelucidatetheinteractionbetweenthepolymersandthesolvents.

1 Experimental

1.1 Materials

The syntheses of P-m,7 and the corresponding monomers have been published[26].In brief,using WCl6-Ph4Sn as a catalyst tolerant of the functional groups on the substitutes of the acetylene monomers,the solution polymerization under optimal conditions yielded the polymers with moderate to high molecular weights (MW).According to the result of1H NMR analysis,the resultant polymers with good stereoregularity are trans-rich(the transcontents are determined to be>80%).Table 1 lists the apparent number-average molecular weight(Mn)and the polydispersity index(PDI)of the samples used in this study.

All the solvents used for the measurements of UV-Vis and fluorescence spectra were high performance liquid chromatography (HPLC)gradeandwereusedasreceived.Thestocksolutionswere prepared by directly dissolving the polymers(or the monomer)in chloroform(C),tetrahydrofuran(THF),dichloromethane(DCM), and acetonitrile(AN).Usually,dodecane(D)is considered as a poor solvent for P-m,7.We prepared the dodecane solutions of P-m,7 with a concentration much lower than the critical aggregation concentration.In preparation,a calculated amount of the concentrated chloroform stock solution was added dropwise into dodecane under vigorous stirring.Since the amount of chloroform is little,its influence can be omitted.

1.2 Measurements

UV-Vis absorption spectra were recorded on a Shimadzu UV-2101 spectrophotometer.The steady-state fluorescence spectra were acquired on a Hitachi F-4500 fluorescence spectrophotometer at room temperature.The slit widths of monochromators for excitation and emission were 10.0 and 5.0 nm,respectively. The time-resolved fluorescence measurements were performed using the time-correlated single-photo counting(TCSPC)technique following excitation by a nanosecond flash lamp(Edinburg Instruments FL900).Fluorescence decay curves were analyzed using the least-squares interactive convolution method.

2 Results and discussion

2.1 UV-Vis absorption and steady state fluorescence spectra

Fig.1(a)shows the UV-Vis absorption spectra of P-m,7 and M-3,7 in chloroform with a concentration of 4×10-6g·mol-1.The absorption band peaked at 295 nm can be assigned to the π-π*transition of the aromatic biphenyl group.However,no clear ab-sorption band at longer wavelength is observed,which implies that the conjugation length of the polyacetylene main chain is not long enough in solutions.The same results can also be obtained in other good solvents,such as tetrahydrofuran,dichloromethane,acetonitrile,and in the poor solvent of dodecane.

Table 1 Molecular characteristics of the P-m,7 samples

Fig.1(b)depicts the fluorescence spectra of the monomer and the polymers dissolved in chloroform with a concentration of 1× 10-5mol·L-1(the molar concentration of the polymer solutions was calculated on the basis of the repeating unit).The spectral shapes of the P-m,7 are found to be almost the same as that of M-3,7,wherein a single emission peak without fine structure is observed.This indicates that the fluorescence emission of the polymers is mainly originated from the side-chain biphenyl group.With regard to the wavelength of emission peak,the effect of the flexible spacer length is not severe.For M-3,7 and the polymer with the longest alkyl spacer(P-9,7),the emission peak locates at 371 nm,while the other three samples present the maximum emission wavelength at 377 nm.In comparison with that of M-3,7,the red-shift observed for the P-2,7,P-3,7,and P-4,7 may be due to the coupling between the side-chain biphenyl group and the polyacetylene backbone.On the other hand,Fig. 1b shows that when the methylene unit number(i.e.,the number m)of the spacer of P-m,7 is decreased from 9 to 2,the fluorescence intensity decreases accordingly.The calculated fluorescence quantum yields in chloroform are 0.281,0.283,0.344,and 0.480 for P-2,7,P-3,7,P-4,7,and P-9,7 with 9,10-diphenylanthracene as the reference,respectively,which are in accordance with the fluores-cence intensity results.Note that the biphenyl groups are chemically linked to the polyacetylene backbone. Shortening the flexible spacer will increase the local concentration of biphenyl groups around the main chain and will restrict the side-chain motion to a certain extent[16].Therefore,in addition to the fluorescence quenching due to the local concentration effect,P-m,7 with shorter spacers can have a stronger resonance energy transfer which can further reduce the emission intensity.

2.2 Solvent effects

To gain an insight into the interaction between the biphenyl group and the solvent molecule,the fluorescence spectra of P-m,7 invarioussolventsweremeasured.As an example,Fig.2(a)shows a set of normalized fluorescence spectra of P-3,7 solutions with a fixed concentration of 1×10-5mol·L-1.In principle,the solvent effects on the fluorescence emission can be quantitatively analyzed by using the Lippert-Matage equation as follows[27-29]:

Δν=νab-νem=2Δf(μE-μG)2/hca3+constant

where Δν is the Stokes shift;νaband νemare the wavenumbers (cm-1)of the absorption and emission,respectively;Δf is the solvent parameter,which is termed as orientation polarizability(Δf= (ε-1)/(2ε+1)-(n2-1)/(2n2+1),where ε and n are the dielectric constant and the refractive index of solvents,respectively);μGand μEare the dipole moments of ground and excited states,respectively.Fig.2(b)gives the plots of the Δν against Δf for P-3,7 and M-3,7 in the solvents of D,C,THF,DCM,and AN.The corresponding fitted results based on the Lippert-Matage equation are also included in Fig.2(b).Obviously,the Stokes shift becomes larger with increasing solvent polarity.This result suggests that the interaction between the solvent and fluorescence group is strengthened with increasing the Δf of solvent,which subsequently causes a decrease of the excited state energy of fluorescent group.From these results,it is reasonable to conclude that the interaction between the solvent and the biphenyl group strengthens with increasing the solvent polarity.

2.3 Lifetime measurements

To get a better understanding of the fluorescence behavior of the polymers and the monomer,their fluorescence decays were measured by using a TCSPC technique.Fig.3 gives the fluorescence decays and the residuals of M-3,7 and P-3,7 in chloroform,respectively.It is found that M-3,7 displays a single exponential decay with a emission lifetime(τ)of 1.44 ns.But for theP-3,7 and also other three polymers,the following triple-exponential function can fit the decay behavior better than the single or double-exponential one does:

y=A1e-t/τ1+A2e-t/τ2+A3e-t/τ3

This reveals that the excited states of the polymers decay through three pathways,namely,there exist three emission centers for the excited state of the polymers.The values of A1,A2, and A3in the function represent the fractions of the number of the molecules decaying in the three pathways.Table 2 summarizes the fitted data of fluorescence decay of M-3,7 and P-m,7.

For the monomer,the single carbon—carbon bond that links the two benzene rings can rotate freely in the dilute solution. Therefore,various conformations can be reached dynamically, giving a single exponential decay of fluorescence.While the biphenyl group is attached to the polyacetylene backbone as a pendant,the excited state energy transferring from the pendant tothebackboneshould be considered[30].Different from the monomer,the rotation of biphenyl group on a side-chain is hindered due to the existences of neighboring side-chains and backbone. Therefore,the fluorescence decay of the polymers becomes complicated.The restricted rotation may result in a component of decay with longer lifetime(τ3in Table 2),which is 6.30,5.33, 5.85,and 3.35 ns for P-2,7,P-3,7,P-4,7,and P-9,7,respectively. It is conceivable that increasing the spacer length will decrease the rotational restriction,and thus the value of τ3of P-9,7 becomes smallest.Compared with that of P-4,7,the τ3value of P-3,7 is smaller,which might be originated from the odd-even effect of the flexible spacer.On the other hand,the fluorescence quenching due to the high local concentration of P-m,7 may result in the fastest decay with a τ1of~0.2 ns.It is worth noting that the dominant lifetime(τ2)of P-m,7 is very close to that of the monomer,which corresponds to a fluorescence relaxation for the energy migration from higher to lower energy levels by the rotation of single carbon—carbon bond between the two benzene rings.We also calculated the mean lifetime τ defined as τ=ΣAiτi,with Aithe relative amplitude of component i.As shownin Table 2,the τ value of P-m,7 decreases with increasing the spacer length.This result supports the physical picture of that the longer spacer can better decouple the interference between the biphenyl group and the backbone.For P-9,7,the fitting data give the dominant lifetime τ2of 1.17 ns,which is even 0.27 ns shorter than that of M-3,7.This observation cannot be well explained at this moment.However,the mean lifetime τ of P-9,7 is almost identical to that of M-3,7.This coincidence suggests that the overall fluorescence behavior of the biphenyl in P-9,7 is similar to that of the monomer,which is also the observation obtained from the steady state fluorescence measurement.

Table 2 Fluorescence lifetime of the samples in chloroform

3 Conclusions

The fluorescence behaviors of a series of biphenyl containing SCLCPA with different lengths of flexible spacers were investigated in various solvents.The fluorescence intensity decreases with decreasing the spacer length from 9 to 2 methylene units, which may be related to the increasing of the local concentration of biphenyl groups.The solvent effect indicates that the interaction between the solvents and the biphenyl groups is strengthened with increasing of the orientation polarizability of the solvents.Time-resolved fluorescence spectra show that the decay of the monomer can be fitted with a single exponential decay, but the polymers demonstrate a triple-exponential decay including three pathways,of which the fastest one is related to the molecular quenching caused by the high local concentration and the slowest one can be ascribed to the rotational restriction of the biphenyl groups.

1 Burroughes,J.H.;Bradley,D.D.C.;Brown,A.R.;Marks,B.N.; Mackay,K.;Friend,R.H.;Burn,P.L.;Holmes,A.B.Nature, 1990,347:539

2 Pei,Q.B.;Yu,G.;Zhang,C.;Yang,Y.;Heeger,A.J.Science, 1995,269:1086

3 Grem,G.;Leditzky,G.;Ullrich,B.;Leising,G.Synthetic Metals, 1992,51:383

4 Liu,J.Z.;Lam,J.W.Y.;Tang,B.Z.Chem.Rev.,2009,109:5799

5 Akagi,K.Chem.Rev.,2009,109:5354

6 Lauchlan,L.;Etemad,S.;Chung,T.C.;Heeger,A.J.;MacDiarmid, A.G.Phys.Rev.B,1981,24:3701

7 Carter,P.W.;Porter,J.D.Phys.Rev.B,1991,43:14478

8 Lee,W.E.;Kim,J.W.;Oh,C.J.;Sakaguchi,T.;Fujiki,M.;Kwak, G.Angew.Chem.Int.Edit.,2010,49:1406

9 Han,C.C.;Balasubramanian,A.J.Polym.Sci.Part A-Polym. Chem.,2008,46:5483

10 Dong,Y.P.;Lam,J.W.Y.;Tang,B.Z.Polym.Mater.Sci.Eng., 2001,84:616

11 Jim,C.K.W.;Qin,A.J.;Lam,J.W.Y.;Hauβler,M.;Tang,B.Z. Polymeric Materials:Science and Engineering,2007,96:414

12 Qin,A.J.;Jim,C.K.W.;Tang,Y.H.;Lam,J.W.Y.;Liu,J.Z.; Mahtab,F.;Gao,P.;Tang,B.Z.J.Phys.Chem.B,2008,112: 9281

13 Scherf,U.;Skothein,T.J.;Elsembaumer,R.L.;Reynolds,J.R. Handbook of conducting polymers.2nd ed.New York:M.Dekker, 1998

14 Huang,H.W.;Horie,K.;Yamashita,T.;Machida,S.;Sone,M.; Tokita,M.;Watanabe,J.;Maeda,Y.Macromolecules,1996,29: 3485

15 He,X.R.;Liu,H.B.;Wang,N.;Ai,X.C.;Wang,S.;Li,Y.L.; Huang,C.S.;Cui,S.;Li,Y.J.;Zhu,D.B.Macromolecular Rapid Communications,2005,26:721

16 Lam,J.W.Y.;Tang,B.Z.Accounts of Chemical Research,2005, 38:745

17 Lam,J.W.Y.;Tang,B.Z.J.Polym.Sci.Part A-Polym.Chem., 2003,41:2607

18 Lam,J.W.Y.;Dong,Y.P.;Law,C.C.W.;Li,Z.;Sun,J.Z.;Chen, H.Z.;Zheng,Q.;Kwok,H.S.;Wang,M.;Feng,X.D.;Shen,J.C.; Tang,B.Z.Macromolecules,2005,38:3290

19 Lam,J.W.Y.;Qin,A.J.;Dong,Y.P.;Lai,L.M.;Haussler,M.; Dong,Y.Q.;Tang,B.Z.J.Phys.Chem.B,2006,110:21613

20 Ye,C.;Xu,G.Q.;Yu,Z.Q.;Lam,J.W.Y.;Jang,J.H.;Peng,H. L.;Tu,Y.F.;Liu,Z.F.;Jeong,K.U.;Cheng,S.Z.D.;Chen,E.Q.; Tang,B.Z.J.Am.Chem.Soc.,2005,127:7668

21 Geng,J.X.;Zhao,X.G.;Zhou,E.L.;Li,G.;Lam,J.W.Y.;Tang, B.Z.Mol.Cryst.Liq.Cryst.,2003,399:17

22 Yu,Z.Q.;Liu,J.H.;Zhu,C.Z.;Chen,E.Q.;Lam,J.W.Y.;Tang, B.Z.Acta Polym.Sin.,2010:783

23 Huang,Y.M.;Lam,J.W.Y.;Cheuk,K.K.L.;Ge,W.K.;Tang,B. Z.Macromolecules,1999,32:5976

24 Huang,Y.M.;Ge,W.K.;Lam,J.W.Y.;Tang,B.Z.Appl.Phys. Lett.,1999,75:4094

25 Yu,Z.Q.;Liu,J.H.;Yan,J.J.;Liu,X.B.;Liang,D.H.;Lam,J.W. Y.;Dong,Y.P.;Li,Z.C.;Chen,E.Q.;Tang,B.Z. Macromolecules,2007,40:8342

26 Lam,J.W.Y.;Kong,X.X.;Dong,Y.P.;Cheuk,K.K.L.;Xu,K. T.;Tang,B.Z.Macromolecules,2000,33:5027

27 Mataga,N.;Kaifu,Y.;Koizumi,M.Bull Chem.Soc.Jpn.,1956, 29:465

28 Lippert,V.E.Z.Electrochem,1957,61:962

29 Lackwicz,J.R.Principles of fluorescence spectroscopy.2nd ed. New York:Plenum Press,1999

30 Ren,Y.;Dong,Y.Q.;Lam,J.W.Y.;Tang,B.Z.;Wong,K.S. Chem.Phys.Lett.,2005,402:468

具有不同长度间隔基的含联苯基团的侧链液晶聚炔的荧光行为

余振强1,2,*张 昕1李子臣1陈尔强1,*
LAM Jacky W.Y.3唐本忠3

(1北京大学化学与分子工程学院高分子科学与工程系,高分子化学与物理教育部重点实验室,北京分子科学国家实验室,北京100871;2深圳大学化学与化工学院,深圳市功能高分子重点实验室,广东深圳 518060;3香港科技大学化学系,香港九龙)

对一系列具有不同长度间隔基的含联苯基团的侧链液晶聚炔的稳态荧光和荧光衰减行为进行了研究.为便于比较,选取其中一个单体作为模型化合物.稳态荧光光谱结果表明,聚合物和单体均显示一个荧光发射,该荧光发射来源于聚合物侧链的联苯基团.随着间隔基长度的减小,聚合物的荧光强度降低.荧光衰减结果表明单体的荧光衰减可以拟合为一个单指数衰减,而聚合物的荧光衰减拟合为三指数衰减.这种三指数衰减可能由溶液局部高浓度引起的猝灭和侧链联苯基团的旋转受阻所引起.溶剂效应表明,溶剂与联苯基团之间的相互作用随溶剂极性增加而增大.

稳态荧光;单取代聚炔;联苯;荧光寿命;溶剂效应

O644

Received:May 13,2010;Revised:July 8,2010;Published on Web:July 9,2010.

*Corresponding authors.YU Zhen-Qiang,Email:zqyu@szu.edu.cn;Tel:+86-755-26535427.CHEN Er-Qiang,Email:eqchen@pku.edu.cn;

Tel:+86-10-62753370.

The project was supported by the National Natural Science Foundation of China(20129001),the Research Grants Council of Hong Kong,China(CA05/06.SC02)and R/D Fund of Shenzhen University,China(200824).

国家自然科学基金(20129001),香港研究资助局(CA05/06.SC02)和深圳大学青年基金(200824)资助项目

ⒸEditorial office of Acta Physico-Chimica Sinica

猜你喜欢

深圳大学侧链联苯
国家药监局关于联苯乙酸凝胶处方药转换为非处方药的公告(2021年第148号)
深圳大学与深圳综合粒子设施研究院签约共建产学研专用线站
《深圳大学学报理工版》2021 年分类总目次
酞菁锌的侧链修饰及光动力活性研究
多溴联苯醚在环境中迁移转化的研究进展
《深圳大学学报理工版》2020年分类总目次
含聚醚侧链梳型聚羧酸盐分散剂的合成及其应用
梳型接枝PVC的性能研究
紫杉醇C13侧链的硒代合成及其结构性质
4,4′-二氯甲基联苯自聚合树脂合成条件优化及表征