Adsorption removal of roxarsone,arsenite(III),and arsenate(V)using iron-modif ied sorghum straw biochar and its kinetics

Shuyan Zang·Yingying Zuo·Juan Wang·Xiuming Liu·Mario Alberto Gomez·Lan Wei

Abstract Arsenic(As)contamination in groundwater is a major problem in many countries,which causes serious health issues.In this paper,a novel method has been developed for the simultaneous removal of ROX and As(III/V)using the modif ied sorghum straw biochar(MSSB).The MSSB was characterized by X-ray diffraction,scanning electron microscopy,Fourier Transform Infrared,and Brunauer–Emmet–Teller(BET)surface area.The removal performance of MSSB for ROX,arsenite[As(III)],and arsenate(As(V))was investigated using batch experiments.At pH of 5,the arsenic concentration of 1.0 mg/L,adsorbent dose of 1.0 g/L,the maximum adsorption capacities of ROX, As(III), and As(V)were 12.4,5.3,and 23.0 mg/g,respectively.The adsorption behaviors were f it well with the Langmuir and the pseudo-second-order rate model.The results showed that MSSB acted as a highly effective adsorbent to simultaneously remove the composite pollution system consisted of ROX and As(III/V)in aqueous solutions,providing a promising method in environmental restoration applications.

Keywords Roxarsone·Arsenic·Arsenate·Sorghum straw biochar·Adsorption

1 Introduction

Arsenic(As)is a persistent,bio-accumulative,toxic element widely distributed in the environment that has been introduced into water or soil by anthropogenic sources(Hao et al.2018;Asere et al.2019),such as mining of arsenic-bearing deposits,discharging of arsenic-containing wastewater,and using of arsenic-containing additives(Yasinta et al.2018;Ali et al.2019;Ng et al.2004).The poisoning effect of arsenic-contaminated drinking water on human health has become more cataclysmic than any other natural catastrophe.Long-term exposure to arsenic-contaminated drinking water even at low levels of exposure,will lead to potential human health hazards,including skin cancer,stomach cancer,respiratory tract cancer,and extensive liver damage(Eisler 2004;Mohanty 2017).In natural waters,arsenic exists in both inorganic and organic forms.Inorganic arsenic is mostly found with trivalent and pentavalent states,known as As(III)and As(V),respectively(Pokhrel and Viraraghavan 2006).As one of the organic arsenic forms,roxarsone(4-hydroxy-3-nitrobenzene arsonic acid,ROX)is used as animal feeding additives for effectively preventing parasitic diseases of poultry.Previous studies indicated that a considerable amount of ROX without metabolization in animals might be released from poultry litter to soil and water(Frensemeier et al.2017;Mahaninia and Wilson 2017;Ji et al.2016;Guzma´n-Fierro et al.2015),which could produce inorganic forms of arsenic,such as As(III)and As(V),displaying even higher toxicity.The mixture of arsenic compounds including both inorganic and organic arsenicals caused environmental contamination(Danish et al.2013).The World Health Organization has been set the standard for arsenic maximum contaminant levels from 50 to 10μg/L since 1993(WHO 2001).To meet stringent drinking water standards,cost-effective arsenic removal technology is urgently needed.

To remove arsenic from the environment,many effective approaches have been developed,such as adsorption(Chandra et al.2010),chemical coagulation-precipitation(Pal et al.2007),ion-exchange(Kim and Benjamin 2004),membrane separation(Seidel et al.2001)and biological treatments(Setyono and Valiyaveettil 2014;Wang et al.2019).Among these methods,adsorption has been used extensively due to its low cost,high removal rate,and relatively mature application(Danish et al.2013).Lowsolubility solid materials with large specif ic surface area and porous structure have mainly served as adsorbents.These adsorbents can provide enough adsorption sites to combine with the pollutants in wastewater(Tian et al.2017;Zhang and Liu 2019)for achieving suff icient control of the water pollution.Biochar(Ocinski et al.2016;Ebrahimi et al.2013;Tian et al.2011;Cheraghi et al.2014)has been commonly used as adsorbents for their advantages,such as large surface area,high stability,the low release of contaminants,recyclability,and inexpensive(Setyono and Valiyaveettil 2014).As one of the primary agricultural wastes with abundant yield,straw is usually discarded or burned directly in the f ield,leading to environmental pollution.Via the straw convention into biocarbon for use as bio-sorbents or adsorbents,is a potentially eff icient way to re-use and recycle this type of agricultural waste(Cheraghi et al.2014).

For the high aff inity of arsenic to iron,different ironloaded sorbents have been made(Iglesias et al.2013;Solesardans et al.2016;Calugaru et al.2019).The solid phases loaded with Fe species would promote the adsorption of arsenates and arsenites and further transformation into stable complexes(Dupont et al.2007).In the practical applications,a series of effective approaches to improve the adsorption capacity of the adsorbent has been reported,in which the adsorbents were modif ied by sintering or doping with different metal ions(Philippova et al.2011;Hossain et al.2016;Ma et al.2015;Su et al.2017).To date,several methods have been reported in the literature about the single adsorption of inorganic arsenic(III,V)or ROX(Kumari et al.2005;Dixit et al.2003,Ustinov and Do 2002;Li et al.2016;Yu et al.2020),however,it is still lacking studies on the simultaneous adsorption of inorganic and organic arsenic(Fu et al.2020).

In this paper,iron-modif ied bio-materials were prepared with sorghum straw biochar.And then,the materials were used to remove inorganic and organic arsenic from synthetic aqueous solutions.The results demonstrated that the as-prepared materials possessed the capability for simultaneous removal of both ROX and As(III/V).Moreover,the use of straw can reduce the cost of removal toxin and provide a promising approach for large-scale use in future applications.The adsorption process of ROX and As(III/V)on the modif ied sorghum straw biochar was further investigated in this paper,including adsorption kinetics,isotherms,and effects of various experimental parameters,which may provide a potential solution to the ROX and As(III/V)contaminated wastewater.

2 Material and methods

2.1 Materials

The chemical reagents used in this work CHOH and KHPOwere spectrum pure and the others were analytical grade.The fresh arsenic working solutions were prepared by diluting the stock arsenate solutions with deionized water.

The sorghum straw biochar was prepared by pyrolysis of sorghum powder with particles size ranging from 40 to 120 mesh under an oxygen-limited condition at 550°C for 1 h.Using X-Ray Fluorescence Spectrometer(XRF,ZSX Primus II)to test the chemical composition of sorghum straw biochar,the results were shown in Table 1.The pH of the solution was adjusted via NaOH and HCl.5 g of sorghum straw biochar was put into 100 mL FeClsolution with a concentration of 0.05 M,and then the mixtures were ultrasonically dispersed for 30 min and stirred for 24 h.The as-obtained solids were washed with deionized water and dried at 60°C for 12 h.At last,the modif ied sorghum straw biochar(MSSB)was obtained.The f low chart of absorbents is shown in Fig.1.

Fig.1 The f low chart of MSSB

Table 1 XRF analysis data

2.2 Batch adsorption experiments

To investigate the adsorption ability of MSSB for mixed arsenic pollutants,batch experiments were carried out.At room temperature,to adsorb arsenic,the pH value of the solution was adjusted with NaOH/HCl,then 0.1 g of MSSB was added to 100 mL mixed solution with 1 mg/L ROX and As(III/V).The adsorption performances of the adsorbent were measured by the removal rate of ROX and As(III/V).In particular,the removal rate of ROX and As(III/V)was characterized by the initial concentration and the f inal concentration of arsenic in the solution.

2.2.1 Arsenic adsorption edges

To investigate the effect of pH value on the adsorption of arsenic by the adsorbent,the batch experiments were conducted at different pH values(from 1.0 to 11.0)by adding NaOH or HCl solution.

2.2.2 Adsorption kinetics

The adsorption equilibrium time was determined by the batch experiments.0.1 g adsorbent was put into a 100 mL with the concentration of ROX and As(III/V)of 1.0 mg/L,and then the mixture was shaken on a platform shaker(150 rpm)at pH=5.0 for different reaction times.The selected reaction time intervals were 0.083,0.25,0.5,1,4,8,12,24,30,36 and 48 h.To measure the concentrations of As,about 1 mL mixture was removed from the vessel at different reaction times,then f iltered with a 0.22μm f ilter.The removal rate(R,%)and the removal capacity(Q,mg/g)of ROX and As(III/V)were calculated using the following equations(Feng et al.2019):

where Cand Care the initial and equilibrium concentrations of ROX and As(III/V),V is the solution volume(L),and m is the mass of the adsorbent(g).

2.2.3 Arsenic adsorption isotherms

To estimate the maximum adsorption capacity of the adsorbent,the adsorption isotherms of MSSB were conducted.The adsorption tests were carried out for the mixed solutions with different initial concentrations C(0.1,1.0,10,20,50 mg/L)of ROX and As(III/V),respectively,and the pH value of the solution was 5.0.Then,0.1 g absorbent was added to each solution and shaken on an orbit shaker at 150 rpm for 48 h.The Langmuir,Freundlich,and Dubinin-Radushkevich isotherms based on the data were obtained from the above experiments under the optimal conditions.

2.2.4 Analytical methods

As(V)was initially reduced to As(III)by thiourea and ascorbic acid(5 g thiourea and 5 g ascorbic acid in 100 mL HO),and then Atomic Fluorescence Spectrophotometer(AFS-HG Hydride generation,AFS-2202E)was used to determine the amount of As(III)in solution.The total inorganic arsenic content was determined by AFS-HG and the concentration of As(V)was calculated by subtraction(Guo et al.2011).

High-performance liquid chromatography(HPLC,Primaide1210)with a C18 reversed-phase column was used to determine the concentration of ROX.The mobile phase was 15%CHOH and 85%KHPO(V/V)buffer solution,the pH value was 3.0,the elution time was 8 min,the detection wavelength was 266 nm and the f low rate was 2.0 mL·min.

The phase and morphology of the adsorbent were characterized by X-ray diffraction(XRD,D8 Quest),Fourier Transform Infrared(FTIR,NICOLET6700),and scanning electron microscopy(SEM,JSM-636OLV).The surface area of the materials was determined by Brunauer–Emmett–Teller(BET)method.The pore size distribution and total volume were calculated by the Brunauer-Joyner-Hallenda(BJH)method applied to the desorption data.

The point of zero charge(pH)of adsorbents was estimated according to the method described by Wang et al.(2019).In detail,the adsorbents were f irst suspended in 0.01 M NaCl until the pH value remained stable.Then,the pH of the suspension was adjusted to different values between 3 and 9 by adding NaOH or HCl.After equilibration for 2 h,the initial pH was recorded.Then,1.5 g NaCl was added into each suspension and the f inal pH was measured after 3 h.The pHwas identif ied as the point at which theΔpH is equal to 0 in the curve ofΔpH vs.the f inal pH.ΔpH was calculated by the difference between the f inal pH and the initial pH.

3 Results and discussion

3.1 Characterization and evaluation of the adsorbent

To analyze the possible adsorption mechanism of ROX and As(III/V)on the adsorbents,the morphology of SSB and MSSB was investigated f irstly.

The SEM images of two absorbents are shown in Fig.2.As shown in Fig.2,the particles of SSB exhibited irregular shapes with smooth surfaces.After modif ication with FeCl,the surface of the adsorbent became rough and uneven.It may be attributed to the surface that was saturated with other particles,such as iron(III)-oxy or hydroxides.The BET measurements showed that the specif ic surface area of the absorbent was 43.39 m/g after Fe-modif ication.After simultaneous adsorption of ROX and As(III/V),the surface of MSSB became rougher,indicating many small particles adhered to the adsorbent surface.The effect may be due to the pores on the adsorbent surface occupied with arsenic ions through complex physical and chemical reactions.The XRD patterns of the MSSB before and after As adsorption are shown in Fig.3.The main peaks of the MSSB before and after As adsorption were assigned to SiO.Furthermore,crystal phases of iron(III)-oxy/hydroxides and As were undetected,indicating that As and iron likely existed in amorphous forms on MSSB(Zhu et al.2020).

Fig.2 S EM of SSB(a),MSSB(b),and MSSB after adsorbed by As(c)

Fig.3 XRD of MSSB(a)and MSSB after adsorbed by As(b)

FTIR analysis of the samples was conducted and the results are shown in Fig.4.The FTIR spectra of the samples were generally similar,indicating that the molecular structure of the straw biochar remained unchanged after modif ication and absorption,besides the appearance of a carbonyl band.The broad peak at 3386 cmin the SSB corresponds to OH/HO group and shifted to 3428 cmafter modif ication.The shift towards lower wavenumbers for OH/HO groups in MSSA may be attributed to the stronger H-bonding that occurs and/or as a result of contributing effects from the amorphous Fe(III)-oxy/hydroxides formed(Lee et al.2010;Gomez et al.2011).It has been reported that large numbers of OH groups in the cellulose on the surface of straw(Ustinov and Do 2002)are benef icial to the adsorption of ROX and As(III/V)for the highly attractive to arsenic ions in solution(Ustinov and Do 2002).After adsorption,the OH/HO on the MSSB changed in relative intensely of well shifted to high wavenumbers,indicating some type of interaction occurred between As and the functional groups of MSSB.An additional band at 3550 cmimplies the additional type of H-bonding interactions occurred in the adsorption process(Lee et al.2010;Gomez et al.2011).It is worth noting that after modif ication,a new band occurred in the MSSB at～1740 cmwhich could be contributing to C=O groups(Gomez et al.2011)but disappeared after adsorption.It possibly indicated that the MSSB containing carboxylate groups or similar functional groups was benef icial to absorb ROX and As(III/V)(Lee et al.2010).The vibrational band at 1577 cmcorresponds to the C=C species in the SSB and shifted towards higher energy(1604 cm)after modif ication which may indicate that groups were strained(Hu et al.2012).After adsorption,a red-shift occurred for these vibrational bands,and the vibrational strength decreased,demonstrating that these groups served as functional adsorption sites of arsenic and could enhance the adsorption ability of arsenic from a solution compared with the previous research(Ansone et al.2013).However,as we have observed here carbonyl and carboxylate groups may also be involved in the adsorption of arsenic.Furthermore,a band at 589 cmcorresponding to the Fe–O stretch vibration(Yang et al.2016)was observed in MSSB,indicating a Fe(III)-oxy/hydroxide was formed on the adsorbent(Lin et al.2019).After adsorption,a new peak at 839 cmcorresponded to As-O stretching shows that As was successfully adsorbed on the surface of the adsorbent(Xie et al.2019).Therefore,based on the vibrational data,the functional groups of OH,C=C,C=O,C–O,and Fe–O on the MSSB may play important roles in effectively binding arsenic from solution.

Fig.4 FTIR spectra of sorghum straw biochar

3.2 Adsorbent performance evaluation

To evaluate the adsorption effect of SSB and MSSB,the removal rates of ROX and As(III/V)in the aqueous system were conducted and the results were shown in Fig.5.From Fig.5,the removal rates of ROX,As(III),and As(V)with the SSB respectively were 18.06%,12.87%,and 34.66%,but they were improved signif icantly to 70.56%,51.66%,and 95.96%by using the MSSB.The signif icant increase in adsorbing ability of MSSB may be attributed to two reasons.One is that the formation of Fe–O through the modif ication of FeClchanged the surface structure of the adsorbent,and the modif ied surface structure enhanced the chemical and/or physical adsorption of the adsorbent.The iron-arsenic co-precipitation(Zhang et al.2019)that occurred on the MSSB could enhance the type of chemisorption.The second reason may be newly formed C=O/COO groups on the MSSB that played an important role in removing arsenic from the solution(Xie et al.2019).These results demonstrated the MSSB obtained from SSB was suitable for the simultaneous co-adsorption of ROX and As(III/V).

3.3 Effect of adsorbent dosage

The effect of MSSB dose on ROX and As(III/V)was investigated for the removal of arsenic is strongly affected by the dosage of the adsorbent(Wang et al.2019;Jahangiri et al.2019).The results were shown in Fig.6.It can be observed that the removal rate for ROX and As(III)increased rapidly with increasing adsorbent dose.In contrast,the removal rate of As(V)is higher than that of As(III)and remains unchanged substantially as the adsorbent dose increased.The higher removal rate of As(V)likely arises from some preferential adsorption sites that may form some relatively stable complexes and/or compounds(Namasivayam and Senthilkumar 1998;Hu et al.2012).When the adsorbent dosage was 0.2 g/L,the removal rate of ROX,As(III),and As(V)were 16.20%,13.81%,and 92.94%,respectively.While the removal rate increased to 70.56%,50.00%,and 96.47%under the adsorbent dosage of 1.0 g/L.The increase in the removal rate may be largely attributed to more adsorbent supplied more adsorption sites(Gupta et al.2005;Murugesan et al.2006).At the MSSB dosage was 1.0 g/L,the adsorption capacities for ROX,As(III),and As(V)were the highest and reached 705.61,500.00,and 964.68 mg/kg,respectively.The adsorbent dose of 1.0 g/L MSSB was used for the subsequent adsorption tests.

Fig.6 Effect of the adsorbent dosage on arsenic removal from ROX and As(III/V),respectively,using 1.0 mg/L As at pH 5 and room temperature

3.4 Effect of temperature

Temperature is another significant factor affect adsorption(Yadav et al.2020).As shown in Fig.7,the removal rates of three pollutants increased first and then decreased with the increasing temperature.The increase of ionic thermal motion could lead to the decrease of binding stability of the adsorbent with arsenic,resulting in the gradual decrease of adsorption capacity on the adsorbent surface(Fan 2013).When it was 25°C,the removal rate of ROX,As(III),and As(V)were the highest,reaching 71.57%,50.79%,and 98.69%,respectively,and the adsorption capacities were 715.7,507.9,and 998.9 mg/kg,respectively.Compared with previous works(Ebrahimi et al.2013;Liu 2007),the larger adsorption capacity observed in this paper indicates that the method may be suitable to remove the combined pollution of As in the water at 25°C.Therefore,the temperature of 25°C was selected,which is more suitable close to practical applications.

3.5 Effect of pH

In general,the pH value can affect the adsorption characteristics of the substrate material since it may lead to changes of arsenic in chemical speciation,solubility,and hydrophilicity.In addition,the adsorption of arsenic is severely affected by zero charge(pH)of the adsorbent.The pHof the MSSB was estimated according to the method described by Wang et al.(Wang et al.2019).Figure 8 shows that the pHvalue of the MSSB is approximately 5.5.The surface charge of the adsorbents is positive at a pH below the pHmeanwhile it is negative when the solution pH is above pH(Wang et al.2019).Considering these two factors,the effect of pH on ROX,As(III)and As(V)removal by MSSB was investigated between 1.0 to 11.0,as shown in Fig.9.

From Fig.9,it can be observed that the removal rates of three As species increased first and then decreased with increasing pH values.At pH=5.0,the removal rates of As(V)and As(III)were the maxima as 99.60%and 62.60%,respectively,and the removal rate of ROX was 71.14%.The uptake of As(V)was remarkably higher than that of ROX and As(III)probably because it was more likely to form stable complexes and/or co-precipitate(Wang et al.2019).At pH=5,As(III)and As(V)exist mainly as HAsOand HAsO/HAsO(Fan et al.2013),and the positive-charged surface adsorbent at pH=5 is beneficial to the adsorption of arsenic in the anion state.At pH=5.5,the surface of the MSSB adsorbent was more negatively charged and disfavored the adsorption of the negative arsenic anions species,inducing the decreased removal rate for pH＞5.The removal rate of ROX appeared the maximum at pH=3.0 and reached close to 100%,which was consistent with the literature(Hu et al.2012).The increased pH leads to increased ionization and hydrophilicity,which would weaken hydrophobic interactions(Hu et al.2012)and thus decrease adsorption,causing its lower removal.Therefore,based on these observations the optimal solution at pH=5 was the default.

Fig.9 Effect of pH on the adsorption of ROX and As(III/V)by MSSB.The adsorbent of 1 g/L at room temperature with an As concentration was 1.0 mg/L

3.6 Adsorption kinetics

Kinetic is an important criterion for the design of a sorption system because it determines the equilibrium time.To conf irm the potential kinetic mechanism of the ROX and As(III/V)sorption on the MSSB,the relationships between time and the removal rate of arsenic were investigated and the result is shown in Fig.10.In general,it can be observed that the adsorption process of ROX and As(III/V)followed the same trend,including two steps,a relatively rapid adsorption step,and a relatively slow adsorption process.It can be attributed to the presence of two diffusion rates(Wang et al.2019),external transport at highly accessible surface adsorption sites and intraparticle transport at less accessible internal adsorption sites of the adsorbent.In the case of ROX,the fast removal process appeared within 4 h and the removal rate reached 67.09%.For As(III)and As(V),the fast removal appeared in 12 h and the removal rate reached 46.84%and 86.93%,respectively.In this step,it could due to the different types of arsenic occupied most of the adsorption sites on the surface of the adsorbent,leading to the fast removal rates(Wang et al.2019).As the reaction time increased and the adsorption sites decreased,the adsorption rates decreased which probably because the adsorption kinetics was dominated by the surface precipitation and intraparticle diffusion at this step.The results were consistent with the previous report(Wang et al.2019).To ensure complete equilibration,an equilibration time of 48 h was selected for the other batch experiments.As shown in Fig.10,the system reached equilibrium within 36 h.

To further investigate the adsorption mechanism of the MSSB for ROX and As(III/V),the pseudo-f irst order and the pseudo-second-order rate equations were f itted to the data.The results are shown in Fig.11 and the parameters obtained from the kinetic model are listed in Table 2.The results demonstrated the pseudo-second-order rate equation based on chemisorption(Sarntanayoot et al.2019;Hubbe et al.2019),which can describe the experimental kinetics data and the rate-limiting steps in this work.The qvalues of ROX,As(III),and As(V)obtained from the pseudosecond-order equation model respectively were 781.25,641.03,and 925.93 mg/kg which were in good agreement with results obtained from the batch isotherm work(Table 3).

Parameters Pseudo-f irst-order Kinetics Pseudo-second-order Kinetics qe(mg/kg) K 1(h-1) R2 qe(mg/kg) K2(kg/(mg h) R2 As(III) 419.02 0.07169 0.9729 641.03 9.73×10–4 0.9929 As(V) 516.39 0.1029 0.9251 925.93 2.43×10–3 0.9985 ROX 467.43 0.9181 0.9386 781.25 1.59×10–3 0.9910

Parameters Langmuir model Freundlich model Dubinin-Radushkevich model qm(mg/kg) KL(L/kg) R2 n KF R2 β(mol2 KJ-2) E(KJ/mol) R2 As(III) 5.3×103 2.14×10–4 0.9935 2.9 1.6499 0.8639 0.6596 0.87 0.9317 As(V) 2.3×104 5.73×10–4 0.9931 1.9 0.1749 0.9560 0.0352 3.77 0.8371 ROX 1.24×104 1.91×10–4 0.9948 2.8 0.5403 0.8899 0.1929 1.61 0.8372

3.7 Adsorption isotherms

To evaluate the adsorption capacities of the MSSB and adsorption mechanism,three isotherms were evaluated(i.e.Langmuir,Freundlich,and Dubinin-Radushkevich)under the optimal adsorption conditions(Uner et al.2016;Solic et al.2020;Langmuir 1917).The results are presented in Table 3.According to Table 3,the models of Freundlich and Dubinin-Radushkevich with the lower correlation coeff icient were not f itted well with experimental data.Langmuir model displayed a higher determination coeff icients(R)in the range of 0.993 to 1.000,and the Langmuir adsorption isotherm for the adsorption of ROX,As(III)and As(V)is shown in Fig.12,indicating Langmuir model was the best-f itted model for ROX and As(III/V)adsorption onto MSSB.The monolayer adsorption represented by the Langmuir isotherm model played an important role in the arsenic removal(Feng et al.2019).The adsorption capacities of ROX,As(III),and As(V)were 12.4,5.3,and 23 mg/g,respectively.The comparison of previous works(Wang et al.2019;Ansone et al.2013;Hu et al.2012;Lu et al.2014),indicates that the adsorption capacities of ROX,As(III),and As(V)by MSSB have been improved signif icantly.Therefore,this method is feasible to simultaneously remove mixed As species,i.e.,ROX,As(III),and As(V),in aqueous systems.

4 Conclusion

In this paper,a novel method has been developed for the simultaneous removal of ROX and As(III/V)synthetic aqueous solutions using low-cost sorghum straw biochar modif ied by FeCl.The optimal parameters of MSSB for the ROX and As(III/V)removal,such as temperature,adsorbent dose,and pH,have been determined.The adsorption mechanism was described by the pseudo-second-order equation and Langmuir isotherm adsorption.Under the optimal conditions,the excellent adsorption capacities of ROX,As(III),and As(V)have been obtained.The results show that low-cost adsorbent material,MSSB possesses a good adsorption effect on arsenic contaminations and great potential for environmental restoration applications.

Acknowledgement

s This work was supported by the National Natural Science Foundation of China(Grant Nos.41773136 and 41703129),Innovation Talent Support Project of Liaoning(Grant No.LR2017073),the National Key Rand D Program of China(No.2017YFD0800301),the basic research projects of Source-sink transformation of arsenic and roxarsone in sediments(XXLJ 2019007).