一种吸附膜的制备及其吸附性能

贾威

摘要：提出一种硅藻土膜制备的方法，利用聚乙烯醇树脂经加热处理后包裹硅藻土经过挤压制备吸附膜对酚酞溶液进行吸附脱色研究。试验结果表明：对酚酞去除率较高，随着聚乙烯醇树脂含量的增加，吸附性能显著提高；并且随着硅藻土的增加，去除率迅速增加，并考察了温度对吸附膜稳定性的影响，

关键词：聚乙烯醇树脂、硅藻土、酚酞、吸附

Preparation and adsorption properties of a kind of adsorption membrane

ABSTRACT：A method of preparation of diatomite membrane is proposed， using polyvinyl alcohol resin after heat treatment package diatomite after extrusion preparation adsorption film of phenolphthalein solution by adsorption decolorization. Test results show that the higher removal rate of phenolphthalein， along with the increase of the content of polyvinyl alcohol resins， adsorption performance is significantly improved； and with the increase of diatomite， the removal rate increased rapidly， and to investigate the effect of temperature on the stability of the adsorbed film.

KEY WORDS：Polyvinyl alcohol resin；diatomite；phenolphthalein， adsorption

一、引言

利用聚乙烯醇树脂能黏结特性，并有一定弹性的黏性将加热溶解的聚乙烯醇树脂与细粉状硅藻土黏结在一起，经过挤压形成有弹性的吸附薄膜。

1、试剂。固体石蜡；聚乙烯醇树脂；硅藻土；添加剂所有化学试剂均为分析纯级。

2、实验方法。先将聚乙烯醇树脂放入烧杯中，在超级恒温水浴箱中加热至90℃左右，待融化后在搅拌器不断搅拌下，加入溶剂油，搅拌均匀后加入硅藻土；再次搅拌均匀后，加入添加剂，搅拌均匀后经过挤压冷却得到产品。

二、分析与讨论

1、聚乙烯醇树脂含量对去除率的影响如图1：

由图中可以看出聚乙烯醇树脂含量增加，去除率增加显著。

2、硅藻土含量对去除率的影响如图2：

由图中可以看出活性炭粉增加到0.55mol/g之后吸附率开始下降。

3、温度对吸附膜稳定性的影响如图3：

由图中可以看出在随着温度的增加，吸附膜的稳定性不断降低，在60℃以下稳定性最好。